Influence of Post Hot Isostatic Pressing on the Microstructural Development and Critical Current Density of YBa2Cu3O7-x

1990 ◽  
Vol 73 (2) ◽  
pp. 450-452 ◽  
Author(s):  
Mesut Aslan ◽  
Herbert Jaeger ◽  
Klaus Schulze ◽  
Arnulf Frisch ◽  
Gunter Petzow
Keyword(s):  
Critical Current Density ◽  
Critical Current ◽  
Current Density ◽  
Hot Isostatic Pressing ◽  
Microstructural Development ◽  
Isostatic Pressing

Improvement of critical current density in the Bi-Pb-Sr-Ca-Cu-O system through hot isostatic pressing

1990 ◽  
Vol 167 (5-6) ◽  
pp. 525-528 ◽  
Author(s):  
S.X. Dou ◽  
H.K. Liu ◽  
M.H. Apperley ◽  
K.H. Song ◽  
C.C. Sorrell ◽  
...  
Keyword(s):  
Critical Current Density ◽  
Critical Current ◽  
Current Density ◽  
Hot Isostatic Pressing ◽  
Isostatic Pressing

Properties of Hot Isostatically Pressed Bi2Sr1.7CaCu2Ox

1992 ◽  
Vol 275 ◽  
Author(s):  
A. S. Nash ◽  
K. C. Goretta ◽  
D. J. Miller ◽  
A. C. Biondo ◽  
Donglu Shi ◽  
...  
Keyword(s):  
Critical Current Density ◽  
Critical Current ◽  
Current Density ◽  
Hot Isostatic Pressing ◽  
Inert Atmosphere ◽  
Preferred Orientation ◽  
Transport Critical Current Density ◽  
Isostatic Pressing

ABSTRACTDense Bi2Sr1.7CaCu2Ox (2212) superconductor pellets were made by hot isostatic pressing in an inert atmosphere. The pellets exhibited a small amount of preferred orientation of the grains. The transport critical current density (Jc) values were very low for all specimens. Dislocations, planar faults, and intergrowths of the Bi2Sr2CuOx phase, which were produced during the pressing, caused the intragranular Jc to increase substantially.