Finite Element Simulation of Stable Fatigue Crack Growth Using Critical CTOD Determined by Preliminary Finite Element Analysis

2014 ◽  
Vol 891-892 ◽  
pp. 1675-1680
Author(s):  
Seok Jae Chu ◽  
Cong Hao Liu
Keyword(s):  
Finite Element ◽  
Fatigue Crack ◽  
Fatigue Crack Growth ◽  
Finite Element Simulation ◽  
Crack Growth ◽  
Crack Tip ◽  
Stress Intensity Factor Range ◽  
Crack Tip Opening Displacement ◽  
Element Analysis ◽  
Element Simulation

Finite element simulation of stable fatigue crack growth using critical crack tip opening displacement (CTOD) was done. In the preliminary finite element simulation without crack growth, the critical CTOD was determined by monitoring the ratio between the displacement increments at the nodes above the crack tip and behind the crack tip in the neighborhood of the crack tip. The critical CTOD was determined as the vertical displacement at the node on the crack surface just behind the crack tip at the maximum ratio. In the main finite element simulation with crack growth, the crack growth rate with respect to the effective stress intensity factor range considering crack closure yielded more consistent result. The exponents m in the Paris law were determined.

Three-dimensional, parallel, finite element simulation of fatigue crack growth in a spiral bevel pinion gear

2005 ◽  
Vol 72 (8) ◽  
pp. 1148-1170 ◽  
Author(s):  
Anı Ural ◽  
Gerd Heber ◽  
Paul A. Wawrzynek ◽  
Anthony R. Ingraffea ◽  
David G. Lewicki ◽  
...  
Keyword(s):  
Finite Element ◽  
Fatigue Crack ◽  
Fatigue Crack Growth ◽  
Finite Element Simulation ◽  
Crack Growth ◽  
Three Dimensional ◽  
Pinion Gear ◽  
Element Simulation ◽  
Parallel Finite Element ◽  
Spiral Bevel

scholarly journals Study on the Influence of the Gurson–Tvergaard–Needleman Damage Model on the Fatigue Crack Growth Rate

Metals ◽  
2021 ◽  
Vol 11 (8) ◽  
pp. 1183
Author(s):  
Edmundo R. Sérgio ◽  
Fernando V. Antunes ◽  
Diogo M. Neto ◽  
Micael F. Borges
Keyword(s):  
Growth Rate ◽  
Fatigue Crack ◽  
Crack Growth Rate ◽  
Fatigue Crack Growth ◽  
Plastic Strain ◽  
Crack Growth ◽  
Damage Model ◽  
Crack Tip ◽  
Strength Parameter ◽  
Stress Intensity Factor Range

The fatigue crack growth (FCG) process is usually accessed through the stress intensity factor range, ΔK, which has some limitations. The cumulative plastic strain at the crack tip has provided results in good agreement with the experimental observations. Also, it allows understanding the crack tip phenomena leading to FCG. Plastic deformation inevitably leads to micro-porosity occurrence and damage accumulation, which can be evaluated with a damage model, such as Gurson–Tvergaard–Needleman (GTN). This study aims to access the influence of the GTN parameters, related to growth and nucleation of micro-voids, on the predicted crack growth rate. The results show the connection between the porosity values and the crack closure level. Although the effect of the porosity on the plastic strain, the predicted effect of the initial porosity on the predicted crack growth rate is small. The sensitivity analysis identified the nucleation amplitude and Tvergaard’s loss of strength parameter as the main factors, whose variation leads to larger changes in the crack growth rate.

Sign in / Sign up

Export Citation Format

Share Document