scholarly journals Physical and Mechanical Properties Evaluation of Corncob and Sawdust Cement Bonded Ceiling Boards

2019 ◽  
Vol 42 ◽  
pp. 65-75 ◽  
Author(s):  
Atoyebi Olumoyewa Dotun ◽  
Odeyemi Samson Olalekan ◽  
Azeez Lateef Olugbenga ◽  
Modupe Abayomi Emmanuel
Keyword(s):  
Mechanical Properties ◽  
Modulus Of Elasticity ◽  
Cement Content ◽  
Physical And Mechanical Properties ◽  
American National Standard Institute ◽  
Mechanical Tests ◽  
Industrial Wastes ◽  
Modulus Of Rupture ◽  
National Standard ◽  
Thickness Swelling

This study considered the production of composite ceiling boards from both agricultural and industrial wastes. Boards with different blending proportions by weight of cement, corncob and sawdust (Cem:Ccb:Swd) were produced and tested. Physical and mechanical tests such as Water Absorption (WA), Thickness Swelling (TS), Modulus of Elasticity (MOE) and Modulus of Rupture (MOR) were carried out on the products. The findings revealed that the board with Cem:Ccb:Swd blending proportion 50:10:40 gave the highest values of MOE and MOR and also had the lowest values of WA and TS. The MOE and MOR values of 3.432 are both higher than the minimum values of 550 N/mm2 and 3 N/mm2 specified for MOE and MOR respectively by the American National Standard Institute, for general-use particle boards. The cement content is inversely proportional to the physical properties and directly proportional to the mechanical properties.

scholarly journals Effects of thermo-hydro-mechanical treatments on various physical and mechanical properties of poplar (Populus) wood

BioResources ◽  
2020 ◽  
Vol 15 (4) ◽  
pp. 9596-9610
Author(s):  
Yali Shao ◽  
Lili Li ◽  
Zhangjing Chen ◽  
Sunguo Wang ◽  
Ximing Wang
Keyword(s):  
Mechanical Properties ◽  
Thermal Treatment ◽  
Modulus Of Elasticity ◽  
Mechanical Treatment ◽  
Elasticity Modulus ◽  
Physical And Mechanical Properties ◽  
Modulus Of Rupture ◽  
Compression Rate ◽  
Thickness Swelling ◽  
Maximum Thickness

Poplar (Populus) wood was subjected in this work to thermo-hydro-mechanical treatment. The influence of the treatment parameters on the physical and mechanical properties were investigated. The wood samples were densified under three compression ratios (0%, 30%, and 50%), and thermally treated at three temperatures (180 °C, 200 °C, and 220 °C), at three thermal treatment durations (3 h, 4 h, and 5 h). The density, modulus of elasticity, modulus of rupture, radial hardness, and thickness swelling were measured. The results showed that the densities of the samples increased by 36.6% to 49.7%. As the compression rate increased, the temperature, duration, modulus of elasticity, modulus of rupture, and hardness increased. However, the dimensions of the densified samples were less stable. Compared to the densified samples, the maximum thickness swelling could be reduced by 74% (from 29.7% to 7.8%) when subjected to a thermal treatment at 220 °C for 3 h.

Particleboard Manufactured with Variation of Press Time

2015 ◽  
Vol 1088 ◽  
pp. 644-647
Author(s):  
Cristiane Inácio de Campos ◽  
Bruno Santos Ferreira ◽  
André Luis Christoforo ◽  
Francisco Antonio Rocco Lahr ◽  
Juliana Cortez Barbosa ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Physical And Mechanical Properties ◽  
Mechanical Tests ◽  
Modulus Of Rupture ◽  
Test Results ◽  
Thickness Swelling ◽  
Mean Values ◽  
Tukey Test ◽  
Press Time ◽  
Brazilian Standard

This research aimed to produce and determine physical and mechanical properties of three-layered particleboard produced with Pinussp. wood particlesand three different times of press, i.e., 3, 5 and 7 minutes. Recommendations of the Brazilian standard ABNT NBR 14810 [1] were adopted to fundament physical and mechanical tests. The properties evaluated were the modulus of rupture (MOR) and modulus of elasticity (MOE) in static bending; internal bond; thickness swelling; water absorption; moisture content and apparent density.The mean values showed, for the physical properties, that all the panels manufactured achievedthe requirements of theBrazilian standard, and for mechanical properties, only the panelsmanufacturedwith 7minutesofpressing timemet therequirements. From the Tukey test results, timesof the pressingcycleinfluencedsignificantlyin allinvestigatedphysical and mechanicalproperties, showed better results the panels madewithseven minutesof the pressingcycle, implyingthat the time ofseven minutesof the pressingcycle is thebest among theinvestigatedperiodsin the manufactureofparticleboard.

scholarly journals Sifat Fisis dan Mekanis Papan Semen dari Serat Tandan Kosong Kelapa Sawit (The Physical and Mechanical Properties of Cement Board Made from Oil Palm Empty Fruit Bunches Fibers)

2016 ◽  
Vol 8 (2) ◽  
pp. 43-52 ◽  
Author(s):  
Djoko Purwanto
Keyword(s):  
Mechanical Properties ◽  
Water Absorption ◽  
Oil Palm ◽  
Modulus Of Elasticity ◽  
Physical And Mechanical Properties ◽  
Modulus Of Rupture ◽  
Thickness Swelling ◽  
Empty Fruit Bunches ◽  
Screw Withdrawal ◽  
Cement Board

Oil palm empty fruit bunches (OPEFB) fiber were industrial waste that has not been widely used by the community, only stacked and cause odors that interfere with the surrounding environment. This research studied the utilization of OPEFB fiber for cement board products using cement as resin and CaCl2 as accelerator. Laboratory scale cement board made from OPEFB fiber were mixed with cement, and CaCl2. The composition of fiber and cement were 1:1, 1:1.5, 1:2, and CaCl2 variations were 0%, 1% and 3%. A mixture of fibers, cement and CaCl2 was compressed at the pressure of 4 ton for 24 hours. The cement boards were tested for physical and mechanical properties according to JIS A 5417-1992, and the results were compared to the requirements of the cement board JIS A 5417-1992. Cement board made from fiber and cement composition 1:1.5 and CaCl2 content 3% produced moisture content, thickness swelling, water absorption, density, modulus of rupture/MOR, modulus of elasticity/MOE and screw withdrawal strength that met the requirement of JIS A 5417-1992. The composition of fiber and cement and the variations of CaCl2 content produced significant effect on water content, water absorption, thickness swelling, modulus of rupture/MOR, modulus of elasticity/MOE and screw withdrawal strength on cement boards.Keywords : oil palm empty fruit bunches fiber, cement boards, physical and mechanical properties

scholarly journals PENGARUH PERENDAMAN PARTIKEL TERHADAP SIFAT FISIS DAN MEKANIS PAPAN PARTIKEL DARI AMPAS TEBU (Saccharum officinarum)

PERENNIAL ◽  
2008 ◽  
Vol 4 (1) ◽  
pp. 6
Author(s):  
Apri Heri Iswanto ◽  
Zahrial Coto ◽  
Kurniawansyah Effendy
Keyword(s):  
Mechanical Properties ◽  
Moisture Content ◽  
Modulus Of Elasticity ◽  
Internal Bond ◽  
Physical And Mechanical Properties ◽  
Saccharum Officinarum ◽  
Hot Water ◽  
Modulus Of Rupture ◽  
Thickness Swelling ◽  
Holding Power

The objective of this research is to research the effect of particle soaking to physical and mechanical properties particleboard that resulted. The best result of particleboard is particleboard with treatment of hot water soaking. From this result obtained average of physical properties of particleboard (i.e. density, moisture content, water absorption, and thickness swelling) are 0.7 g/cm3; 9.58%; 52.27%; 10.05%. While the result average of mechanical properties of particleboard (i.e. Modulus of Rupture, Modulus of Elasticity, Internal Bond and Screw Holding Power) are 118.79 kg/cm2; 8.909 kg/cm2; 1.85 kg/cm2; 28.40 kg. Key words: Soaking, bagasse, particleboard, physical and mechanical properties References

SIFAT FISIK MEKANIK PAPAN PARTIKEL TANPA PEREKAT DARI TANDAN KOSONG KELAPA SAWIT (Elaeis Guineensis acq)

2014 ◽  
Vol 6 (1) ◽  
pp. 15 ◽  
Author(s):  
Budi Tri Cahyana
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Water Content ◽  
Oil Palm ◽  
Modulus Of Elasticity ◽  
Physical And Mechanical Properties ◽  
Modulus Of Rupture ◽  
Particle Board ◽  
Thickness Swelling ◽  
Empty Fruit Bunches

This research aimed to get the physical and mechanical properties of non adhesive-particle board from oil palm empty fruit bunches. The oil palm empty fruit bunches were degradated to fibre and boiled in boiling water during 60 minute then dried in ± 2 weeks. The dried raw material was chopped to be fibre in 5 mesh, 10 mesh, and 16 mesh. It were complied into a mold and then hot pressed in 35 kgf/cm2 pressure during 10 minute with 3 of temperature variety, 160°C, 180°C and 200°C. The result showed that the average of particle board water content was 7,11 -  9,85 % and the density was 0,63 – 0,76 gr/cm3. The highest thickness swelling was 22,59 % in 10 mesh and 160 0C (a2b1) temperature of oil palm empty fruit bunches. The modulus of rupture was 211,67 kg/cm2  in 10 mesh and 180 0C (a2b2) temperature. The modulus of elasticity was 490,85 kg/cm2 in 10 mesh and 160 0C (a2b1) temperature. The tensile strength was 7,49 kg/cm2 in 5 mesh and 200 0C (a1b3) temperature. The average of physical and mechanical properties such as water content, density, modulus of rupture, tensile strength were fulfill the SNI requirement, while the average of thickness swelling and modulus of elasticity were not fulfill the SNI requirement.Keywords: oil palm empty fruit bunches, particle board

Medium Density Particleboard with Addition of Impregnated Paper

2014 ◽  
Vol 1025-1026 ◽  
pp. 543-546
Author(s):  
Juliana Cortez Barbosa ◽  
Anderson Luiz da Silva Michelon ◽  
Elen Aparecida Martines Morales ◽  
Cristiane Inácio de Campos ◽  
André Luis Christoforo ◽  
...  
Keyword(s):  
Moisture Content ◽  
Modulus Of Elasticity ◽  
Mechanical Tests ◽  
Modulus Of Rupture ◽  
Medium Density ◽  
Test Results ◽  
Thickness Swelling ◽  
Adhesion Test ◽  
Layer Medium ◽  
Determine Moisture Content

The aim of this research was to produce three-layer Medium Density Particleboard (MDP), with the addition of impregnated paper, in the inner layer, in proportions of 1; 5 and 20%. In this study, MDP was composed with particles of small size in outer layers, and larger particles in internal layer. After panel manufacturing, physical and mechanical tests based on Brazilian Code ABNT NBR 14.810 were carried out to determine moisture content; density; thickness swelling; water absorption; modulus of rupture (MOR) and modulus of elasticity (MOE) in static bending and internal adhesion. Test results were compared to commercial panels, produced with 100% Eucalyptus, considering the requirements specified by Brazilian Code. Properties presented values close to normative specifications, indicating positively the possibility of production of MDP using addition of waste paper impregnated.

scholarly journals ADSORPTION OF NANOWOLLASTONITE ON CELLULOSE SURFACE: EFFECTS ON PHYSICAL AND MECHANICAL PROPERTIES OF MEDIUM-DENSITY FIBERBOARD (MDF)

CERNE ◽  
2016 ◽  
Vol 22 (2) ◽  
pp. 215-222 ◽  
Author(s):  
Hamid Reza Taghiyari ◽  
Roya Majidi ◽  
Asghar Jahangiri
Keyword(s):  
Mechanical Properties ◽  
Density Functional ◽  
Medium Density Fiberboard ◽  
Physical And Mechanical Properties ◽  
Mechanical Tests ◽  
National Standard ◽  
Medium Density ◽  
Wood Fibers ◽  
Strong Adsorption ◽  
Cellulose Surface

ABSTRACT Effects of nanowollastonite (NW) adsorption on cellulose surface were studied on physical and mechanical properties of medium-density fiberboard (MDF) panels; properties were then compared with those of MDF panels without NW-content. The size range of NW was 30-110 nm. The interaction between NW and cellulose was investigated using density functional theory (DFT). Physical and mechanical tests were carried out in accordance with the Iranian National Standard ISIRI 9044 PB Type P2 (compatible with ASTM D1037-99) specifications. Results of DFT simulations showed strong adsorption of NW on cellulose surface. Moreover, mechanical properties demonstrated significant improvement. The improvement was attributed to the strong adsorption of NW on cellulose surface predicted by DFT, adding to the strength and integrity between wood fibers in NW-MDF panels. It was concluded that NW would improve mechanical properties in MDF panels as a wood-composite material, as well as being effective in improving its biological and thermal conductivity.

scholarly journals KUALITAS PAPAN KOMPOSIT LIMBAH KULIT BATANG SAGU (Metroxylon sp) DAN PLASTIK POLIPROPILENA BERDASARKAN JUMLAH LAPISAN PENYUSUN

2018 ◽  
Vol 7 (1) ◽  
Author(s):  
Mayang Archila ◽  
Farah Diba ◽  
Dina Setyawati ◽  
. Nurhaida
Keyword(s):  
Mechanical Properties ◽  
Moisture Content ◽  
Physical And Mechanical Properties ◽  
Modulus Of Rupture ◽  
Internal Bonding ◽  
Thickness Swelling ◽  
Composite Board ◽  
Average Value ◽  
Composite Layers ◽  
Sago Bark

The objective of this research is to evaluate the effect of the number of composite layers on the quality of the composite board from sago bark waste and plastic waste, and the number of composite layers that produce the best quality on composite board. The composite board is made with size 30 cm x 30 cm x 1 cm. The composition and division of the material was carried out manually with the polypropylene distribution divided into three parts: the front and rear respectively of 15%, and the center 70% of the plastic weight. Target density of composite boards was 0.7 g / cm3. The treatment used is based on the number of layers composing, which is 5 layers, 7 layers, 9 layers, 11 layers and 13 layers. After mixed the sago bark particle and waste of polypropylene, the materials then compressed with hot press at 180oC with pressure about ± 25 kg / cm2 for 10 minutes. The composite boards then tested the quality included physical and mechanical properties. Testing of physical and mechanical properties refers to JIS A 5908-2003 standard. Physical properties consist of density, moisture content, thickness swelling, and water absorption. Mechanical properties consist of modulus of rupture, modulus of elasticity, internal bonding, and modulus of screw holding strength. The study used a completely randomized design experiment consisting of 5 treatments and 3 replications. The results showed the average value of composite density was range between 0.6962 – 0.7896 g/cm3, the moisture content was range between 4.3388 % - 6.8066%, the thickness swelling was range between 8.2605% - 11.9615%, and water absorption was range between 17.2380% - 22.3867%. The average value of modulus of rupture was range between 60,0632 kg/cm2 – 64,4068 kg/cm2, the modulus of elasticity was range between 17935,1813g/cm2 – 32841,8278 kg/cm2, the internal bonding was range between 1,9268 kg/cm2  - 5,4119 kg/cm2, and the modulus of screw holding strength was range between 78,2530 kg/cm2 – 92,9677 kg/cm2. The composite board made from sago stem bark waste and polypropylene waste plastic with 13 layers treatment is the best composite board and fulfilled the JIS A 5908-2003 standard. Keywords: bark of sago, composite boards, layer of composite, polypropylenes plastic, waste

scholarly journals Relationships between Thermoplastic Type and Properties of Polymer-Triticale Boards

Polymers ◽  
2019 ◽  
Vol 11 (11) ◽  
pp. 1750 ◽  
Author(s):  
Radosław Mirski ◽  
Pavlo Bekhta ◽  
Dorota Dziurka
Keyword(s):  
Mechanical Properties ◽  
Modulus Of Elasticity ◽  
Bending Strength ◽  
Physical And Mechanical Properties ◽  
Thickness Swelling ◽  
Hydrophobic Properties ◽  
Pine Wood ◽  
Moisture Contents ◽  
The Face

This study examined the effects of selected types of thermoplastics on the physical and mechanical properties of polymer-triticale boards. The investigated thermoplastics differed in their type (polypropylene (PP), polyethylene (PE), polystyrene (PS)), form (granulate, agglomerate) and origin (native, recycled). The resulting five-ply boards contained layers made from different materials (straw or pine wood) and featured different moisture contents (2%, 25%, and 7% for the face, middle, and core layers, respectively). Thermoplastics were added only to two external layers, where they substituted 30% of straw particles. This study demonstrated that, irrespective of their type, thermoplastics added to the face layers most favorably reduced the hydrophobic properties of the boards, i.e., thickness, swelling, and V100, by nearly 20%. The bending strength and modulus of elasticity were about 10% lower in the experimental boards than in the reference ones, but still within the limits set out in standard for P7 boards (20 N/mm2 according to EN 312).

scholarly journals INFLUENCE OF THERMAL MODIFICATION ON THE PHYSICAL AND MECHANICAL PROPERTIES OF Eucalyptus badjensis MIXED PARTICLEBOARD / OSB PANELS

FLORESTA ◽  
2021 ◽  
Vol 51 (2) ◽  
pp. 419
Author(s):  
Giuliano Ferreira Pereira ◽  
Setsuo Iwakiri ◽  
Rosilani Trianoski ◽  
Polliana D'angelo Rios ◽  
Renan Zunta Raia
Keyword(s):  
Mechanical Properties ◽  
Water Absorption ◽  
Phenol Formaldehyde ◽  
Physical And Mechanical Properties ◽  
Dry Mass ◽  
Thermal Modification ◽  
Modulus Of Rupture ◽  
Thickness Swelling ◽  
Swelling Properties ◽  
Different Temperatures

The objective of this research was to evaluate the effects of thermal modifications, at different temperatures and exposure times, on the technological properties of mixed particleboard / OSB panels made out of Eucalyptus badjensis. Using the wood of Eucalyptus badjensis, Particleboard, OSB and mixed Particleboard/OSB panels (control and thermally modified) were manufactured. The mixed panels’ thermal modification was carried out under three temperatures (180ºC, 200ºC and 220ºC) and two exposure times (10 minutes and 12 minutes). For the panels’ manufacturing, 6% of phenol-formaldehyde adhesive and 1% of paraffin were employed, which was calculated based on the particles’ dry mass. The water absorption and thickness swelling properties were evaluated after 2 and 24 hours of immersion, in addition to the panels’ modulus of elasticity, modulus of rupture and internal bond. Based on the results, we were able to conclude that the thermal modification affected most of the physical properties positively. From the different exposure times studied, the most effective one was the period of 12 minutes, especially for water absorption after 2 hours, which caused a reduction of 11.27%. In turn, the most effective temperature was of 220ºC, highlighting the thickness swelling after 24 hours, which caused a swelling decrease of 23.76% in comparison with the control panels. Regarding the mechanical properties, the thermal modification, in terms of the studied exposure times and temperatures, did not affect the results of the mixed particleboard /OSB panels. 