The size range of mineral and ceramic particles of one to a few microns is awkward to prepare for examination by TEM. Electrons can be transmitted through smaller particles directly and larger particles can be thinned by crushing and dispersion onto a substrate or by embedding in a film followed by ion milling. Attempts at dispersion onto a thin film substrate often result in particle aggregation by van der Waals attraction. In the present work we studied 1-10 μm diameter Al2O3 spheres which were transformed from the amprphous state to the stable α phase.After the appropriate heat treatment, the spherical powders were embedded in as high a density as practicable in a hard EPON, and then microtomed into thin sections. There are several advantages to this method. Obviously, this is a rapid and convenient means to study the microstructure of serial slices. EDS, ELS, and diffraction studies are also considerably more informative. Furthermore, confidence in sampling reliability is considerably enhanced. The major negative feature is some distortion of the microstructure inherent to the microtoming operation; however, this appears to have been surprisingly small. The details of the method and some typical results follow.