Aging effects on interfacial reactions between Cu addition into the Sn-9Zn lead-free solder and Au substrate

Author(s):  
Wei-Kai Liou ◽  
Yee-Wen Yen ◽  
Chien-Chung Jao
2007 ◽  
Vol 22 (10) ◽  
pp. 2663-2667 ◽  
Author(s):  
Yee-wen Yen ◽  
Wei-kai Liou

This study investigates interfacial reactions of (Sn–9Zn) + xCu/Ni systems. Ni5Zn21, Cu5Zn8, (Ni,Zn,Cu)3Sn4, (Cu,Ni,Zn)6Sn5, and Cu6Sn5 phases were formed on the Sn–9Zn/Ni interface at 240–270 °C, when 0–10 wt% Cu was added to the Sn–9Zn solder. Experimental results indicate that changing the concentration of Cu in the Sn–9Zn solder dramatically changes the formation of intermetallic compounds (IMCs) in the (Sn–9Zn) + xCu/Ni system. Different diffusion and segregation rates of elements are the main reasons for a change in the IMC evolution.


Author(s):  
Yifei Zhang ◽  
Zijie Cai ◽  
Jeffrey C. Suhling ◽  
Pradeep Lall

The microstructure, mechanical response, and failure behavior of lead free solder joints in electronic assemblies are constantly evolving when exposed to isothermal aging and/or thermal cycling environments. In our prior work on aging effects, we have demonstrated that the observed material behavior variations of Sn-Ag-Cu (SAC) lead free solders during room temperature aging (25°C) and elevated temperature aging (125°C) were unexpectedly large and universally detrimental to reliability. Such effects for lead free solder materials are especially important for the harsh applications environments present in high performance computing and in automotive, aerospace, and defense applications. However, there has been little work in the literature, and the work that has been done has concentrated on the degradation of solder ball shear strength (e.g. Dage Shear Tester). Current finite element models for solder joint reliability during thermal cycling accelerated life testing are based on traditional solder constitutive and failure models that do not evolve with material aging. Thus, there will be significant errors in the calculations with the new lead free SAC alloys that illustrate dramatic aging phenomena. In the current work, we have extended our previous studies to include a full test matrix of aging temperatures and solder alloys. The effects of aging on mechanical behavior have been examined by performing stress-strain and creep tests on four different SAC alloys (SAC105, SAC205, SAC305, SAC405) that were aged for various durations (0–6 months) at room temperature (25°C), and several elevated temperatures (50, 75, 100, and 125°C). Analogous tests were performed with 63Sn-37Pb eutectic solder samples for comparison purposes. Variations of the mechanical and creep properties (elastic modulus, yield stress, ultimate strength, creep compliance, etc.) were observed and modeled as a function of aging time and aging temperature. In this paper, we report on the creep results. The chosen selection of SAC alloys has allowed us to explore the effects of silver content on aging behavior (we have examined SACN05 with N = 1%, 2%, 3%, and 4% silver; with all alloys containing 0.5% copper). In order to reduce the aging induced degradation of the material behavior of the SAC alloys, we are testing several doped SAC alloys in our ongoing work. These materials include SAC0307-X, SAC105-X, and SAC305-X; where the standard SAC alloys have been modified by the addition of small percentages of one or more additional elements (X). Using dopants (e.g. Bi, In, Ni, La, Mg, Mn, Ce, Co, Ti, etc.) has become widespread to enhance shock/drop reliability, and we have extended this approach to examine the ability of dopants to reduce the effects of aging and extend thermal cycling reliability.


Author(s):  
S. M. Kamrul Hasan ◽  
Abdullah Fahim ◽  
Jeffrey C. Suhling ◽  
Sa’d Hamasha ◽  
Pradeep Lall

Abstract Lead free electronic assemblies are often subjected to thermal cycling during qualification testing or during actual use. The dwell periods at the high temperature extreme during thermal cycling cause thermal aging phenomena in the solder material, including microstructural evolution and material property degradation. In addition, lead free solders can also experience aging effects during the ramp periods between the low and high temperature extremes of the cycling. In this study, the mechanical behavior evolution occurring in SAC305 lead free solder subjected to various thermal cycling exposures has been investigated. Uniaxial test specimens were prepared by reflowing solder in rectangular cross-section glass tubes with a controlled temperature profile. After reflow solidification, the samples were placed into the environmental chamber and thermally cycled from −40 C to +125 C under a stress-free condition (no load). Several thermal cycling profiles were examined including: (1) 90 minute cycles with 15 minutes ramps and 30 minutes dwells, (2) air-to-air thermal shock exposures with 30 minutes dwells and near instantaneous ramps, (3) 30 minute cycles with 15 minutes ramps and no dwells (saw tooth profile), (4) 150 minute cycles with 45 minutes ramps and 30 minutes dwells, and (5) no cycling (simple aging at the high temperature extreme). For each profile, 10–15 samples were cycled for various durations of cycling (e.g. 48, 96, and 240 cycles), which were equivalent to various aging times at the high temperature extreme of T = 125 C. After cycling, the stress-strain curves and mechanical properties including effective elastic modulus and Ultimate Tensile Strength (UTS) of all the cycled samples were measured. For each cycling profile, the evolutions of the mechanical properties were characterized as a function of the cycling duration, as well as the net aging time at the high temperature extreme. Comparison of the results of various thermal cycling profiles showed that the detrimental effects of aging are accelerated in a thermal cycling environment. Furthermore, microstructure evolution during thermal cycling has also been investigated to validate the observed mechanical properties degradation. The test results revealed that the mechanical properties degradation of SAC305 are higher in thermal cycling compared to simple equivalent aging. For example, the elastic modulus and UTS of SAC305 reduced by 41%, and 38%, respectively after 5 days aging whereas these properties reduced by 69%, and 51%, respectively after 5 days equivalent aging using thermal cycling profile #4 (240 cycles).


Author(s):  
Hongtao Ma ◽  
Tae-Kyu Lee ◽  
Dong Hyun Kim ◽  
H G Park ◽  
Sang Ha Kim ◽  
...  

Author(s):  
Mohammad Hasnine ◽  
Muhannad Mustafa ◽  
Jeffrey C. Suhling ◽  
Barton C. Prorok ◽  
Michael J. Bozack ◽  
...  

Author(s):  
Jing Wu ◽  
Mohammad S. Alam ◽  
Jeffrey C. Suhling ◽  
Pradeep Lall

Abstract Aging effects are common in lead free solder joints within electronic assemblies that are exposed to isothermal environments for extended periods. Such exposures lead to evolution of the solder microstructure, which results in changes in the mechanical properties and creep behavior of the solder joints. In our recent investigations, we have been utilizing Scanning Electron Microscopy (SEM) to better understand aging induced degradations. The microstructural evolutions were observed in SAC305 and SAC_Q (SAC+Bi) alloys exposed to isothermal conditions at T = 125 °C for several different regions from several different joints. The microstructures in several fixed regions of interest were recorded after predetermined time intervals of aging, which were 1 hour (up to 24 hours) and 10 hours (up to 150 hours) for the short term aging samples; and 250 hours (up to 2500 hours) for the long term aging samples. Using the recorded images and imaging processing software, the area and diameter of each IMC particle was tracked during the aging process. As expected, the quantitative analysis of the evolving SAC_Q microstructure showed that the particles coalesced during aging leading to a decrease in the number of particles. This caused an increase in the average diameter of the particles of slightly more than 100% for long term aging of 2500 hours. For SAC305, the average particle diameter was found to increase at three times the rate (increase of 200% after 2500 hours of aging). Thus, coarsening of IMC particles was greatly mitigated in the SAC_Q alloy relative to that observed in SAC305. Immediately after reflow solidification, Bismuth rich phases were present in the SAC_Q joints. During aging at T = 125 °C, the bismuth was observed to quickly go into solution both within the beta-Sn dendrites and in the intermetallic rich regions between dendrites. This resulted in solid solution strengthening of the lead free solder. It was also found that the aging-induced presence of bismuth in solution within the beta-Sn matrix provided an increased resistance to the Ostwald ripening diffusion process that coarsens the Ag3Sn IMC particles. The combination of these two effects in the SAC+Bi alloy lead to greatly improved resistance to aging induced effects relative to the SAC305 solder alloy. Finally, we have compared the time dependent evolution of microstructure with the degradation in strength during aging for of the two solder alloys, and good correlations were observed.