scholarly journals Nano-Surface Composite Coating Reinforced by Ta2C, Al2O3 and MWCNTs Nanoparticles for Aluminum Base via FSP

Coatings ◽  
2021 ◽  
Vol 11 (12) ◽  
pp. 1496
Author(s):  
Essam B. Moustafa ◽  
Waheed Sami Abushanab ◽  
Ammar Melaibari ◽  
Anastasia V. Mikhaylovskaya ◽  
Mohamed Shaaban Abdel-Wahab ◽  
...  
Keyword(s):  
Aluminum Alloy ◽  
Wear Behavior ◽  
Composite Layer ◽  
Wear Properties ◽  
2024 Aluminum Alloy ◽  
Advanced Technique ◽  
Multi Wall Carbon Nanotubes ◽  
Friction Stir ◽  
Surface Composite ◽  
Al 2024

In the present work, an advanced technique was applied to coat an Al 2024 alloy with a surface composite layer reinforced with various nanoparticles. The surface of Al 2024 aluminum alloy was modified with Ta2C, Al2O3 and multi wall carbon nanotubes MWCNTs nanoparticles by friction stir process (FSP). An improvement in the surface of the fabricated nanocomposite due to the refinement of the microstructure grains was achieved. In addition, a significant improvement in the hardness and wear behavior was observed. The reinforcement particles were incorporated into double and triple hybrid composite particles to determine the most effective combination for the controlled properties. The results showed that for the composite reinforced with a double hybrid of Al2O3 and MWCNTs, the microstructure grains of the fabricated nanocomposite surface were refined by 40 times. The hardness was significantly improved, i.e., it was increased by 48% by incorporating the triple reinforcement (Ta2C, Al2O3, and MWCNTs) into the surface of Al 2024 aluminum alloy. The results of wear properties were in agreement with the results of hardness; the maximum wear resistance was obtained for Al 2024-Ta2C + Al2O3 + MWCNTs, and the wear rate was reduced by 11 times.

Wear Assessment of Ti/SiC Surface Nano-Composite Layer and its Associated CP-Ti Substrate

2012 ◽  
Vol 445 ◽  
pp. 595-600 ◽  
Author(s):  
Ali Shamsipur ◽  
Seyed Farshid Kashani-Bozorg ◽  
Abbas Zarei Hanzaki
Keyword(s):  
Surface Layer ◽  
Wear Behavior ◽  
Composite Layer ◽  
Pure Titanium ◽  
Commercially Pure Titanium ◽  
Micro Hardness ◽  
Wear Properties ◽  
Friction Stir ◽  
Pin On Disc ◽  
Cp Ti

In the present investigation, the surface of a commercially pure titanium (CP-Ti) substrate was modified to Ti/SiC nanocomposite layer employing friction stir processing technique; nanosized SiC powder was introduced into the stir zone provided by a rotating and advancing tool. The fabricated nanocomposite surface layer exhibited a micro hardness value of ~535HV which is much greater than 160HV of the substrate material using Vickers micro hardness testing. In addition, the un-treated CP-Ti substrate showed sever wear regime in the pin-on-disc test against the hardened AISI 52100 steel. It suffers extensive typical adhesive wear dominated by plastic deformation as evidenced by scanning electron microscopy. Also, deep grooves were formed, i.e. evidence of abrasive wear. Contrary to this, enhanced wear properties were detected for the Ti/SiC nanocomposite surface layer, i.e. lower coefficient of friction and weight loss. The nanocomposite surface layer was found to be adherent to the underlying substrate during the pin-on-disc test. The superior wear behavior of the nanocomposite surface layer is attributed to its improved micro hardness value due to the presence of hard nanosize SiC particles in a refined titanium matrix.

Friction stir welding of 2024 aluminum alloy: Study of major parameters and threading feature on probe

2017 ◽  
Vol 31 (11) ◽  
pp. 5435-5445 ◽  
Author(s):  
Sarah Gholam Nejad ◽  
Mehdi Yektapour ◽  
Arash Akbarifard
Keyword(s):  
Aluminum Alloy ◽  
Friction Stir Welding ◽  
2024 Aluminum Alloy ◽  
Friction Stir

Microstructure and Wear Properties of In Situ TiC-Cr7C3/Fe Surface Composite

2011 ◽  
Vol 415-417 ◽  
pp. 170-173
Author(s):  
Jing Wang ◽  
Si Jing Fu ◽  
Yi Chao Ding ◽  
Yi San Wang
Keyword(s):  
Sliding Wear ◽  
Wear Behavior ◽  
Wear Test ◽  
Dry Sliding Wear ◽  
Dry Sliding ◽  
Test Machine ◽  
Wear Properties ◽  
Surface Composite ◽  
The Matrix

A wear resistant TiC-Cr7C3/Fe surface composite was produced by cast technique and in-situ synthesis technique. The microstructure and dry-sliding wear behavior of the surface composite was investigated using scanning electron microscope(SEM), X-ray diffraction(XRD) and MM-200 wear test machine. The results show that the surface composite consists of TiC and Cr7C3as the reinforcing phase, α-Fe and γ-Fe as the matrix. The surface composite has excellent wear-resistance under dry-sliding wear test condition with heavy loads.

Evaluation of microstructure and wear behavior of friction stir processed cast aluminum alloy

2012 ◽  
Vol 63 ◽  
pp. 90-97 ◽  
Author(s):  
Sima Ahmad Alidokht ◽  
Amir Abdollah-zadeh ◽  
Soheil Soleymani ◽  
Tohid Saeid ◽  
Hamid Assadi
Keyword(s):  
Aluminum Alloy ◽  
Wear Behavior ◽  
Cast Aluminum Alloy ◽  
Cast Aluminum ◽  
Friction Stir
Sign in / Sign up

Export Citation Format

Share Document