A Comparative Study of Two-Layer NiAl Bond Coat TBC and its Failure Mechanism

2007 ◽  
Vol 336-338 ◽  
pp. 1770-1772
Author(s):  
He Fei Li ◽  
Zhao Hui Zhou ◽  
Hesnawi A ◽  
Kuo Jiang ◽  
Sheng Kai Gong
Keyword(s):  
Electron Beam ◽  
Comparative Study ◽  
Thermal Cycling ◽  
Failure Mechanism ◽  
Thermal Barrier Coatings ◽  
Vapor Deposition ◽  
Bond Coat ◽  
Physical Vapor Deposition ◽  
Thermal Barrier ◽  
Barrier Coatings

Thermal barrier coatings with one-layered/ two-layered NiAl bond coat were produced by electron beam physical vapor deposition (EB-PVD). Compared to the TBC with one-layered bond coat, the TBC with two-layered bond coat improved the thermal cycling resistance significantly. The failure mechanism of the two-layer NiAl bond coat TBC was investigated in this paper.

scholarly journals Isothermal Oxidation Behavior of Gadolinium Zirconate (Gd2Zr2O7) Thermal Barrier Coatings (TBCs) produced by Electron Beam Physical Vapor Deposition (EB-PVD) technique

2018 ◽  
Vol 16 (1) ◽  
pp. 986-991 ◽  
Author(s):  
Kadir Mert Doleker ◽  
Yasin Ozgurluk ◽  
Hayrettin Ahlatci ◽  
Abdullah Cahit Karaoglanli
Keyword(s):  
Electron Beam ◽  
Thermal Barrier Coatings ◽  
Vapor Deposition ◽  
Bond Coat ◽  
Physical Vapor Deposition ◽  
Isothermal Oxidation ◽  
Atmospheric Plasma ◽  
Thermal Barrier ◽  
Barrier Coatings ◽  
X Ray

AbstractThermal Barrier Coatings (TBCs) provide thermal insulation for gas turbine components operating at high temperatures. Generally, TBCs were produced on a MCrAlY bond coat with 7-8% Yttria Stabilized Zirconia (YSZ) using Atmospheric Plasma Spray (APS) technique. In this study, Inconel 718 substrate material was coated with CoNiCrAlY bond coat using high velocity oxygen fuel (HVOF) technique. Afterward, Gd2Zr2O7 was deposited on samples using Electron Beam Physical Vapor Deposition (EB-PVD) technique. Produced TBCs were exposed to isothermal oxidation tests at 1000°C for 8 h, 24 h, 50 h and 100 h in muffle furnace. Scanning electron microscopy-energy distribution X-ray (SEM-EDX) spectroscopy was used to investigate thermally grown oxide (TGO) layer and TGO growth behavior of TBCs. In addition, X-ray Diffractometer (XRD) analysis was performed to TBCs to understand whether phase transformation occurs or not before and after oxidation.

Strain Tolerance and Microstructure of Thermal Barrier Coatings Produced by Electron Beam Physical Vapor Deposition Process

2006 ◽  
Vol 522-523 ◽  
pp. 267-276 ◽  
Author(s):  
Kunihiko Wada ◽  
Yutaka Ishiwata ◽  
Norio Yamaguchi ◽  
Hideaki Matsubara
Keyword(s):  
Electron Beam ◽  
High Temperature ◽  
Thermal Barrier Coatings ◽  
Vapor Deposition ◽  
Physical Vapor Deposition ◽  
Aging Treatment ◽  
Nanoindentation Test ◽  
Thermal Barrier ◽  
Barrier Coatings ◽  
Strain Tolerance

Several kinds of thermal barrier coatings (TBCs) deposited by electron beam physical vapor deposition (EB-PVD) were produced as a function of electron beam power in order to evaluate their strain tolerance. The deposition temperatures were changed from 1210 K to 1303 K depending on EB power. In order to evaluate strain tolerances of the EB-PVD/TBCs, a uniaxial compressive spallation test was newly proposed in this study. In addition, the microstructures of the layers were observed with SEM and Young’s moduli were measured by a nanoindentation test. The strain tolerance in as-deposited samples decreased with an increase in deposition temperature. In the sample deposited at 1210 and 1268 K, high-temperature aging treatment at 1273 K for 10 h remarkably promoted the reduction of the strain tolerance. The growth of thermally grown oxide (TGO) layer generated at the interface between topcoat and bondcoat layers was the principal reason for this strain tolerance reduction. We observed TGO-layer growth even in the as-deposited sample. Although the thickness of the initial TGO layer in the sample deposited at high temperature was thicker, the growth rate during aging treatment was smaller than those of the other specimens. This result suggests that we can improve the oxidation resistance of TBC systems by controlling the processing parameters in the EB-PVD process.