High rate fabrication of copper and copper–gold electrodes by laser-induced selective electroless plating for enzyme-free glucose sensing

In the current study, the method of Selective Surface Activation Induced by Laser (SSAIL) was used for the fabrication of metallic and bimetallic structures based on copper and gold on the surface of glass and glass-ceramics.

Preparation, characterization, and catalytic performance of Pd–Ni/AC bimetallic nano-catalysts

Palladium–nickel (Pd–Ni) bimetallic nano-catalysts supported on activated carbon (Pd–Ni/AC) have been successfully prepared by impregnation method enhanced with ultrasonic. The prepared Pd–Ni/AC catalysts were used for the catalytic hydrodechlorination reaction of bleached shellac and characterized by Fourier-transform infrared spectroscopy, nitrogen adsorption, X-ray diffraction, X-ray photoelectron spectroscopy, field-emission scanning electron microscope, and high-resolution transmission electron microscopy. The results show that Pd–Ni bimetallic structures in catalytic particles with the diameter of 4 and 14 nm were distributed uniformly on AC support, and the lattice fringe spacing in catalytic particles was measured as 0.213 nm which is lying in the region between monometallic Pd (111; 0.225 nm) and Ni (111; 0.203 nm), and that Pd1–Ni1/AC catalyst exhibits the best catalytic hydrodechlorination performance with the dechlorination efficiency of 92.58 wt% while it is used for the hydrodechlorination of bleached shellac, and the optimum catalytic performance is related to the synergistic electronic effect and bimetallic structure of the Pd1–Ni1/AC sample.