Boswellia sacra Extract-Loaded Mesoporous Bioactive Glass Nano Particles: Synthesis and Biological Effects

Bioactive glasses (BGs) are being increasingly considered for numerous biomedical applications. The loading of natural compounds onto BGs to increase the BG biological activity is receiving increasing attention. However, achieving efficient loading of phytotherapeutic compounds onto the surface of bioactive glass is challenging. The present work aimed to prepare novel amino-functionalized mesoporous bioactive glass nanoparticles (MBGNs) loaded with the phytotherapeutic agent Boswellia sacra extract. The prepared amino-functionalized MBGNs showed suitable loading capacity and releasing time. MBGNs (nominal composition: 58 wt% SiO2, 37 wt% CaO, 5 wt% P2O5) were prepared by sol-gel-modified co-precipitation method and were successfully surface-modified by using 3-aminopropyltriethoxysilane (APTES). In order to evaluate MBGNs loaded with Boswellia sacra, morphological analysis, biological studies, physico-chemical and release studies were performed. The successful functionalization and loading of the natural compound were confirmed with FTIR, zeta-potential measurements and UV-Vis spectroscopy, respectively. Structural and morphological evaluation of MBGNs was done by XRD, SEM and BET analyses, whereas the chemical analysis of the plant extract was done using GC/MS technique. The functionalized MBGNs showed high loading capacity as compared to non-functionalized MBGNs. The release studies revealed that Boswellia sacra molecules were released via controlled diffusion and led to antibacterial effects against S. aureus (Gram-positive) bacteria. Results of cell culture studies using human osteoblastic-like cells (MG-63) indicated better cell viability of the Boswellia sacra-loaded MBGNs as compared to the unloaded MBGNs. Therefore, the strategy of combining the properties of MBGNs with the therapeutic effects of Boswellia sacra represents a novel, convenient step towards the development of phytotherapeutic-loaded antibacterial, inorganic materials to improve tissue healing and regeneration.

Ion-doped mesoporous bioactive glass: preparation, characterization, and applications using the spray pyrolysis method

Bioactive glasses (BAG) are one type of biomaterial that is used in dentistry and orthopedics to repair or replace damaged bone. The spray pyrolysis process is low-cost and one of the most common ways for producing porous films and films with high-density packing and particle homogeneity.

Incorporation of Zinc into Binary SiO2-CaO Mesoporous Bioactive Glass Nanoparticles Enhances Anti-Inflammatory and Osteogenic Activities

During the healing and repair of bone defects, uncontrolled inflammatory responses can compromise bone regeneration. Biomaterials with anti-inflammatory activity are favorable for bone tissue regeneration processes. In this work, multifunctional Zn-containing mesoporous bioactive glass nanoparticles (Zn-MBGs) exhibiting favorable osteogenic and anti-inflammatory activities were produced employing a sol-gel method. Zn-MBGs exhibited a mesoporous spherical shape and nanoscale particle size (100 ± 20 nm). They were degradable in cell culture medium, and could release Si, Ca, and Zn in a sustained manner. Zn-MBGs also exhibited a concentration-dependent cellular response. The extract of Zn-MBGs obtained by incubation at 0.1 mg/mL (in culture medium) for 24 h could enhance in vitro mineralization, alkaline phosphatase activity, the expression of osteogenesis-related genes, and the production of intracellular protein osteocalcin of rat bone marrow stromal cells (BMSCs). Moreover, the extract of Zn-MBGs at 0.1 mg/mL could significantly downregulate the expression of inflammatory genes and the production of inducible nitric oxide in RAW 264.7 cells, particularly under stimulation of inflammatory signals interferon-γ (IFN-γ) and lipopolysaccharide (LPS). Zn-MBGs also inhibited the pro-inflammatory M1 polarization of RAW264.7 cells induced by LPS and IFN-γ. In summary, we successfully synthesized Zn-MBGs with concentration-dependent osteogenic and anti-inflammatory activities. Zn-MBGs show their great potential in immunomodulation strategies for bone regeneration, representing a multifunctional biomaterial that can be applied to regenerate bone defects under inflammatory conditions.

Effect of mesoporous bioactive glass on odontogenic differentiation of human dental pulp stem cells

Healthy pulp tissue plays an important role in normal function and long-term retention of teeth. Mesoporous bioactive glass (MBG) as a kind of regenerative biomaterials shows the potential in preserving the vital pulp. In this study, MBG prepared by organic template method combined with sol-gel method were used in human dental pulp cell culture and ectopic mineralization experiment. Real-Time PCR was used to explore its ability to induce odontogenic differentiation of dental pulp cells. MBG and rat crowns were implanted under the skin of nude mice for 4 weeks to observe the formation of pulp dentin complex. We found that MBG can release Si and Ca ions and has a strong mineralization activity in vitro. The co-culture of MBG with human dental pulp cells promoted the expression of DMP-1 (dentin matrix protein-1) and ALP (alkalinephosphatase) without affecting cell proliferation. After 4 weeks of subcutaneous implantation in nude mice, the formation of hard tissue with regular structure under the material could be seen, and the structure was similar to dentin tubules. These results indicate that MBG can induce the differentiation of dental pulp cells and the formation of dental pulp-dentin complex and has the potential to promote the repair and regeneration of dental pulp injuries.

The Antibacterial and Remineralization Effect of Silver-Containing Mesoporous Bioactive Glass Sealing and Er-YAG Laser on Dentinal Tubules Treated in a Streptococcus mutans Cultivated Environment

The aim of this study was to evaluate the remineralization and antibacterial effect of silver-containing mesoporous bioactive glass (MBG-Ag) sealing combined with Er:YAG laser irradiation on human demineralized dentin specimens in a Streptococcus mutans cultivated environment. A total of 48 human dentin specimens were randomly divided into four groups. The characteristics of MBG-Ag and the occlusion efficiency of the dentinal tubules were analyzed using X-ray diffraction patterns, Fourier-transform infrared spectroscopy, scanning electron microscope images and energy dispersive X-ray spectroscopy. Moreover, the antibacterial activity against Streptococcus mutans was evaluated by colony formation assay. The results showed that the dentin specimens with Er:YAG laser irradiation can form a melted occlusion with a size of 3–4 µm. MBG-Ag promoted the deposition of numerous crystal particles on the dentinal surface, reaching the deepest penetration depth of 70 μm. The results suggested that both MBG-Ag and laser have the ability to enhance the remineralization and precipitation of hydroxyapatite crystals. While the results showed that MBG-Ag sealing combined with the thermomechanical subablation mode of Er:YAG laser irradiation-induced dense crystalline deposition, reaching a penetration depth of more than 300 µm, silver nanoparticles without good absorption of the Er:YAG laser resulted in a heterogeneous radiated surface. Er:YAG laser irradiation with a low energy and pulse rate cannot completely inhibit the growth of S. mutans, but MBG-Ag sealing reached the bactericidal concentration. It was concluded that the simultaneous application of MBG-Ag sealing and Er:YAG laser treatment can prevent the drawbacks of their independent uses, resulting in a superior form of treatment for dentin hypersensitivity.