A simple preparation route for polysilicate titanium salt from spent titanium solutions

Polysilicate titanium salt (PST) is synthesized by using spent titanium solutions and polysilicic acid (PSiA) as raw materials. PSiA could improve the aggregation ability of titanium salt flocculants and also restrain the hydrolysis of Ti4+ to stabilize titanium salts. Meanwhile, replacing titanium salt with spent titanium solutions could reduce the cost of PST and solve the problem of wastewater treatment in the titanium industry, which makes valuable waste regeneration possible. Scanning electron microscopy (SEM) results show the morphology transformation (sheet, spheroid, and sphere) of PST with different Ti/Si molar ratios. The formation process of PST is analyzed by Fourier transform infrared spectroscopy (FT-IR) and X-ray photoelectron spectroscopy (XPS). This study investigates the effect of Ti/Si molar ratios on PST flocculation performance in humic–kaolin water and actual domestic wastewater treatment. The in situ floc size change of PST is measured by laser particle size analyzer in humic–kaolin water treatment. Additionally, the performance of PST is comprehensively evaluated on flocculation and sedimentation ability, rapid sweep netting ability and stability. In short, the prepared PST in this study is suitable for treating wastewater with high turbidity and chemical oxygen demand (COD) in a wide range of pH values.

Composition and Performance of Nanostructured Zirconium Titanium Conversion Coating on Aluminum-Magnesium Alloys

Nanostructured conversion coating of Al-Mg alloy was obtained via the surface treatment with zirconium titanium salt solution at 25°C for 10 min. The zirconium titanium salt solution is composed of tannic acid 1.00 g·L−1, K2ZrF60.75 g·L−1, NaF 1.25 g·L−1, MgSO41.0 g/L, and tetra-n-butyl titanate (TBT) 0.08 g·L−1. X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and Fourier transform infrared spectrum (FT-IR) were used to characterize the composition and structure of the obtained conversion coating. The morphology of the conversion coating was obtained by atomic force microscopy (AFM) and scanning electron microscopy (SEM). Results exhibit that the zirconium titanium salt conversion coating of Al-Mg alloy contains Ti, Zr, Al, F, O, Mg, C, Na, and so on. The conversion coating with nm level thickness is smooth, uniform, and compact. Corrosion resistance of conversion coating was evaluated in the 3.5 wt.% NaCl electrolyte through polarization curves and electrochemical impedance spectrum (EIS). Self-corrosion current density on the nanostructured conversion coating of Al-Mg alloy is9.7×10-8A·cm-2, which is only 2% of that on the untreated aluminum-magnesium alloy. This result indicates that the corrosion resistance of the conversion coating is improved markedly after chemical conversion treatment.