Mechanical Properties, Fatigue Life, and Electrical Conductivity of Cu-Cr-Hf Alloy after Equal Channel Angular Pressing

2017 ◽  
Vol 20 (1) ◽  
pp. 1700536
Author(s):  
Daria V. Shangina ◽  
Vladimir F. Terent'ev ◽  
Dmitry V. Prosvirnin ◽  
Olga V. Antonova ◽  
Natalia R. Bochvar ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Electrical Conductivity ◽  
Fatigue Life ◽  
Equal Channel Angular Pressing ◽  
Angular Pressing

Effect of Aging Treatment on Mechanical Properties and Electrical Conductivity of Cu-5.7%Cr In Situ Composite Produced by Equal Channel Angular Pressing

2012 ◽  
Vol 560-561 ◽  
pp. 344-348 ◽  
Author(s):  
Wei Wei ◽  
Kun Xia Wei ◽  
Igor V. Alexandrov ◽  
Qing Bo Du ◽  
Jing Hu
Keyword(s):  
Mechanical Properties ◽  
Electrical Conductivity ◽  
Equal Channel Angular Pressing ◽  
Aging Treatment ◽  
In Situ Composite ◽  
Angular Pressing ◽  
Peak Aging ◽  
Average Size ◽  
Equiaxed Grains

The effect of aging treatment on mechanical properties and electrical conductivity of Cu-5.7%Cr in situ composite produced by equal channel angular pressing (ECAP) was investigated here. The rotation and spreading of Cr particles was observed in Cu-5.7%Cr alloy during the ECAP, resulting in long thin in situ filaments. The equiaxed grains of the Cu phase with an average size of 200 nm were developed after eight passes of ECAP. When aging at 400~450 °C for 1 h, Cu-5.7%Cr composite after ECAP shows the maximum microhardness, and the electrical conductivity is larger than 70% of IACS. At 400 °C, the peak aging time appears for 0.5~2 h, dependent on the pre-strain for all ECAP samples. With the increase of ECAP passes, the enhancement of tensile strength due to the aging treatment declines, and even shows negative after eight passes of ECAP. The combination of ECAP and aging treatment would be a promising process to balance mechanical properties and electrical conductivity of Cu-5.7%Cr composite.

Mechanical Properties of Different Coppers Processed by Equal Channel Angular Pressing

2010 ◽  
Vol 667-669 ◽  
pp. 713-718 ◽  
Author(s):  
Oscar Fabián Higuera ◽  
Jairo Alberto Muñoz ◽  
Jose María Cabrera
Keyword(s):  
Mechanical Properties ◽  
Heat Treatment ◽  
Electrical Conductivity ◽  
Equal Channel Angular Pressing ◽  
Room Temperature ◽  
Angular Pressing ◽  
Cu Alloys ◽  
Ecap Process ◽  
First Pass ◽  
Annealing Heat Treatment

Mechanical properties of two Cu alloys (electrolytic and fire refined) severely deformed by equal channel angular pressing (ECAP) process were investigated. They were treated with a annealing heat treatment to 600°C during 30 minutes and then they were extruded in a Φ=90º ECAP die at room temperature following route Bc. Heavy deformation was introduced in the samples after a considerable number of ECAP passes from 1, 2, 3, 4, 5, 6, 7, 8, to 16. The principal changes were introduced in the first pass by ECAP but a gradual increment in the mechanical properties was observed for the consecutive ECAP passes. Also, the electrical conductivity decreased with increasing numbers of ECAP passes.

scholarly journals Effects of equal channel angular pressing and heat treatments on the microstructures and mechanical properties of selective laser melted and cast AlSi10Mg alloys

2021 ◽  
Vol 21 (3) ◽  
Author(s):  
Przemysław Snopiński ◽  
Mariusz Król ◽  
Marek Pagáč ◽  
Jana Petrů ◽  
Jiří Hajnyš ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Low Temperature ◽  
Equal Channel Angular Pressing ◽  
Heat Treatments ◽  
Electron Backscattered Diffraction ◽  
Angular Pressing ◽  
Low Temperature Annealing ◽  
Transmission Electron ◽  
Before And After ◽  
The Impact

AbstractThis study investigated the impact of the equal channel angular pressing (ECAP) combined with heat treatments on the microstructure and mechanical properties of AlSi10Mg alloys fabricated via selective laser melting (SLM) and gravity casting. Special attention was directed towards determining the effect of post-fabrication heat treatments on the microstructural evolution of AlSi10Mg alloy fabricated using two different routes. Three initial alloy conditions were considered prior to ECAP deformation: (1) as-cast in solution treated (T4) condition, (2) SLM in T4 condition, (3) SLM subjected to low-temperature annealing. Light microscopy, transmission electron microscopy, X-ray diffraction line broadening analysis, and electron backscattered diffraction analysis were used to characterize the microstructures before and after ECAP. The results indicated that SLM followed by low-temperature annealing led to superior mechanical properties, relative to the two other conditions. Microscopic analyses revealed that the partial-cellular structure contributed to strong work hardening. This behavior enhanced the material’s strength because of the enhanced accumulation of geometrically necessary dislocations during ECAP deformation.