SINTERING BEHAVIOR AND MICROWAVE DIELECTRIC PROPERTIES OF NOVEL LOW TEMPERATURE FIRING Bi3FeMo2O12 CERAMIC
2011 ◽
Vol 01
(04)
◽
pp. 379-382
◽
Keyword(s):
In the present work, a novel low temperature firing Bi 3 FeMo 2 O 12 ceramic was synthesized via the solid-state reaction method. The monoclinic Bi 3 FeMo 2 O 12 phase can be formed at a low temperature 670°C. A relative density above 96% can be obtained when sintering temperature is above 800°C. The Bi 3 FeMo 2 O 12 ceramic sintered at 845°C for 2 h shows high microwave dielectric performance with a permittivity ~27.2, a Qf value of 14,500 GHz and a temperature coefficient of -80 ppm/°C. It might be a candidate for low temperature co-fired ceramics technology.
2010 ◽
Vol 663-665
◽
pp. 1028-1031
2004 ◽
Vol 449-452
◽
pp. 729-732
◽
2011 ◽
Vol 239-242
◽
pp. 77-80
◽
2013 ◽
Vol 03
(04)
◽
pp. 1320003
◽
2012 ◽
Vol 472-475
◽
pp. 2107-2110
◽
2012 ◽
Vol 512-515
◽
pp. 1198-1202
2010 ◽
Vol 663-665
◽
pp. 608-611
2011 ◽
Vol 148-149
◽
pp. 887-890
2021 ◽
2012 ◽
Vol 24
(5)
◽
pp. 1505-1510
◽