scholarly journals PENGARUH PENGGUNAAN ZEOLIT SEBAGAI BAHAN PENGGANTI SEBAGIAN SEMEN TERHADAP KUAT TEKAN PAVING BLOCK KONVENSIONAL

2019 ◽  
Vol 10 (2) ◽  
pp. 35-40
Author(s):  
Agung Rizki Pratomo ◽  
Fepy Supriani ◽  
Agustin Gunawan
Keyword(s):  
Compressive Strength ◽  
Conventional Method ◽  
Strength Test ◽  
Test Results ◽  
Compressive Strength Test

This research was motivated by the contained SiO2 in zeolite. The purpose of this research was to know the zeolite effect as a substitute of cement in constructing 14 days paving block material which used conventional method toward the compressive strength of paving block. This research used SNI 03-06-1996 in constructing and testing the materials. The material was cube shaped with ±5 cm size which consists of normal paving block and 6 variations with 5 specimens of each variation. Total of specimen were 35. Substitute of zeolite variations used 2,5%, 5%, 7,5%, 10%, 12,5%, and 15% on the weight of cement. The result of compressive strength of normal paving block is 15,64 MPa. The result of compressive strength test had increased in the variation of 2,5% zeolite substitute by 6,28% normal paving block. The result of compressive strength test results showed the greatest decrease in variation of 15% zeolite replacement by 39,05% against normal paving block. 

scholarly journals Analysis of The Rock Fracture on Uniaxial Compressive Strength Test

2021 ◽  
Vol 2 (1) ◽  
Author(s):  
Edward Dinoy ◽  
Yohanes Gilbert Tampaty ◽  
Imelda Srilestari Mabuat ◽  
Joseph Alexon Sutiray Dwene
Keyword(s):  
Compressive Strength ◽  
Uniaxial Compressive Strength ◽  
Poisson Ratio ◽  
Rock Fracture ◽  
Strength Test ◽  
Maximum Pressure ◽  
Test Results ◽  
Average Value ◽  
Compressive Strength Test ◽  
Uniaxial Compressive Strength Test

The compressive strength test is one of the technical properties or compressive strength tests that are commonly used in rock mechanics to determine the collapse point or the elasticity of rock against maximum pressure. The rock collapse point is a measure of the strength of the rock itself when the rock is no longer able to maintain its elastic properties. The purpose of this test is to find out how long the rock maintains its strength or elasticity properties when pressure is applied, and to find out the difference between the strength of compact rock and rock that has fractures when pressure is applied. Rocks that have fractures will break more easily or quickly when pressure is applied compared to compact rocks. This analysis is carried out by comparing the rock strength of each sample, both those that have fractures and compact rocks. To find out these differences, laboratory testing was carried out. The test results show the value (compressive strength test 57.76 MPa), (elastic modulus 5250.000MPa), (Poisson ratio 0.05) and the average value of rock mechanical properties test (axial 0.91), (lateral-0.279), and (volumetric 0.252) . Based on the test results above, it shows that rocks that have fractures will break more easily when pressure is applied, compared to compact rocks that have a long time in the uniaxial compressive strength test.

scholarly journals Effect of fine recycled aggregates on the properties of non-cement blended materials

2020 ◽  
Vol 323 ◽  
pp. 01018
Author(s):  
Wei-Ting Lin ◽  
Lukáš Fiala ◽  
An Cheng ◽  
Michaela Petříková
Keyword(s):  
Compressive Strength ◽  
Blast Furnace Slag ◽  
Interface Structure ◽  
Strength Test ◽  
Recycled Aggregates ◽  
Test Results ◽  
Granulated Blast Furnace Slag ◽  
Fine Aggregates ◽  
Compressive Strength Test ◽  
Furnace Slag

In this study, the different proportions of co-fired fly ash and ground granulated blast-furnace slag were used to fully replace the cement as non-cement blended materials in a fixed water-cement ratio. The recycled fine aggregates were replaced with natural fine aggregates as 10%, 20%, 30%, 40% and 50%. The flowability, compressive strength, water absorption and scanning electron microscope observations were used as the engineered indices by adding different proportions of recycled fine aggregates. The test results indicated that the fluidity cannot be measured normally due to the increase in the proportion of recycled fine aggregates due to its higher absorbability. In the compressive strength test, the compressive strength decreased accordingly as the recycled fine aggregates increased due to the interface structure and the performance of recycled aggregates. The fine aggregates and other blended materials had poor cementation properties, resulting in a tendency for their compressive strength to decrease. However, the compressive strength can be controlled above 35 MPa of the green non-cement blended materials containing 20% recycled aggregates.

scholarly journals THE EFFECT OF ADDING CEMENT WASTE ON THE QUALITY OF CONCRETE COMPRESSIVE

Jurnal CIVILA ◽  
2021 ◽  
Vol 6 (2) ◽  
pp. 213
Author(s):  
Asrul Majid ◽  
Hammam Rofiqi Agustapraja
Keyword(s):  
Compressive Strength ◽  
Strength Test ◽  
Fine Aggregate ◽  
Infrastructure Development ◽  
Test Results ◽  
Compressive Strength Test ◽  
Compressive Strength Of Concrete ◽  
Concrete Materials ◽  
Test Objects

Infrastructure development is one of the important aspects of the progress of a country where most of the constituents of infrastructure are concrete. The most important constituent of concrete is cement because its function is to bind other concrete materials so that it can form a hard mass. The large number of developments using cement as a building material will leave quite a lot of cement bags.In this study, the authors conducted research on the effect of adding cement waste to the compressive strength of concrete. This study used an experimental method with a total of 24 test objects. The test object is in the form of a concrete cylinder with a diameter of 15 cm and a height of 30 cm and uses variations in the composition of the addition of cement waste cement as a substitute for fine aggregate, namely 0%, 2%, 4% and 6%. K200). The compressive strength test was carried out at the age of 7 days and 28 days.The test results show that the use of waste as a partial substitute for fine aggregate results in a decrease in the compressive strength of each mixture. at the age of 7 days the variation of 2% is 16.84 MPa, 4% is 11.32 MPa and for a mixture of 6% is 6.68 MPa. Meanwhile, the compressive strength test value of 28 days old concrete in each mixture decreased by ± 6 MPa. So the conclusion is cement cement waste cannot be used as a substitute for fine aggregate in fc 16.6 (K200) quality concrete because the value is lower than the specified minimum of 16.6 MPa.

Degradation Phenomenon of Basic Mechanical Properties of Plain Reactive Powder Concrete with Time

2014 ◽  
Vol 1065-1069 ◽  
pp. 1871-1874
Author(s):  
Xiao Fei Wang ◽  
Yang Ping Wang ◽  
Li Cheng Wu
Keyword(s):  
Compressive Strength ◽  
Uniaxial Compressive Strength ◽  
Strength Test ◽  
Hot Water ◽  
Reactive Powder Concrete ◽  
Test Results ◽  
Compressive Strength Test ◽  
Water Curing ◽  
Uniaxial Compressive Strength Test ◽  
Reactive Powder

The same batch reactive powder concrete specimens were obtained with same raw materials and curing process, uniaxial compressive strength test had been done on the specimens after hot water curing placed in laboratory for seven days , three months and three years. The test results showed that seven-day strength and three-month strength of plain reactive powder concrete after hot water curing are almost equal. Strength of plain reactive powder concrete has not degradation within three months after hot water curing. While strength of plain reactive powder appears serious degradation phenomenon after placed in Laboratory for three years. Comparing uniaxial compressive strength test results of plain reactive powder concrete at three-month with three-year after hot water curing ,we find that strength of plain reactive concrete at three-year decrease about 27 percent than the strength of plain reactive powder concrete placed at laboratory for three months, and elasticity modulus increases about 71 percent, axial peak strain decrease about 62 percent respectively .With the passage of time, plain reactive powder concrete appears more Brittle Features and less toughness.

scholarly journals Impact of Incorporating Metakaolin on the Mechanical Performance of High Grade Concrete

2019 ◽  
Vol 8 (3) ◽  
pp. 7736-7739 ◽  
Keyword(s):  
Compressive Strength ◽  
Flexural Strength ◽  
Mechanical Performance ◽  
Strength Test ◽  
Strength Development ◽  
High Grade ◽  
Test Results ◽  
Normal Concrete ◽  
Split Tensile Strength ◽  
Compressive Strength Test

This paper studies the effect of incorporating metakaolin on the mechanical properties of high grade concrete. Three different metakaolins calcined at different temperature and durations were used to make concrete specimens. Three different concrete mixtures were characterized using 20% metakaolin in place of cement. A normal concrete mix was also made for comparison purpose. The compressive strength test, split tensile test and flexural strength tests were conducted on the specimens. The compressive strength test results showed that all the metakaolin incorporated concrete specimens exhibited higher compressive strength and performed better than normal concrete at all the days of curing. The rate of strength development of all the mixes was also studied. The study revealed that all the three different metakaolin incorporated mixtures had different rate of strength development for all the days of hydration (3, 7,14, 28, 56 and 90), indicating that all the metakaolins possessed different rate of pozzolanic reactivity. Further, from the analysis of the test results, it was concluded that the variation in the rate of strength development is due to the differences in the temperature and duration at which they were manufactured. The results of split tensile strength test and the flexural strength test conducted on the specimens, supported the conclusions drawn from the results of compressive strength test. The paper also discusses, the rate of development of compressive strength and the pozzolanic behaviour of the metakaolins in light of their parameters of calcination and physical properties such as amorphousness and particle size. This paper has been written with a view to make the potential of metakaolin available to the construction industry at large

scholarly journals KEKUATAN TEKAN MATERIAL SPOILER MOBIL BERBASIS KOMPOSIT ROTAN EPOKSI

POROS ◽  
2018 ◽  
Vol 16 (1) ◽  
Author(s):  
Agustinus Purna Irawan
Keyword(s):  
Compressive Strength ◽  
Product Development ◽  
Free Market ◽  
Strength Test ◽  
Reinforced Composites ◽  
Test Results ◽  
Compressive Strength Test ◽  
The Difference ◽  
Strength Difference

This study aims to obtain the compressive strength of the material of a car spoiler product that was developed using materials from rattan fiber epoxy reinforced composites material. The car spoiler products are car accessories that also function as one of the equipment related to aerodynamics. The study was conducted by making test samples of rattan fiber epoxy reinforced composites and compared with the compressive strength of plastic spoiler materials obtained from the free market. The testing standard used is the compressive strength test of ASTM D 695. Based on the test results obtained compressive strength of spoiler made of plastic is 47.68 ± 1.37 MPa and rattan fiber epoxy reinforced composites material is 43.49 ± 4.21 MPa, with a compressive strength difference of 8.8%. The compressive strength of modeling results obtained a compressive strength of 47.97 MPa. This result is quite good and the difference is quite small, so the results of the study can be used as a reference for further product development.

scholarly journals Shellac dan Gelatin untuk Konsolidasi Artefak Kayu

2021 ◽  
Vol 15 (2) ◽  
pp. 44-58
Author(s):  
Leliek Agung Haldoko
Keyword(s):  
Compressive Strength ◽  
Color Change ◽  
Fungal Growth ◽  
Strength Test ◽  
Optimum Concentration ◽  
Test Results ◽  
Test Parameters ◽  
Compressive Strength Test ◽  
Consolidation Material ◽  
Test Color

Wood is a hygroscopic organic material, prone to damage and weathering, especially by humidity. The moisture in the wood will trigger biotic activities such as fungus, which can decompose of wood materials, that is, cellulose. Moreover, wood is susceptible to insect attacks such as termites. This condition will cause the wood to become brittle so that the strength of the wood will decrease. To strengthen brittle wood, consolidation treatments are needed. Material for wood consolidation that has been used is Paraloid B72 with acetone solvent, which is not easy to find everywhere Materials tested for wood artifacts consolidations were shellac and gelatin with a concentration of 5%, 7,5%, and 10%. As a comparison, the material used for wood consolidation is Paraloid B72 10%. Test parameters used include SEM test, density test, compressive strength test, color change test, fungal growth observation, and FTIR test. Test results have shown that shellac 7,5% and 10% can be an alternative to Paraloid B72 as a wood artifacts consolidation material. Shellac 7,5% is the optimum concentration for wood artifacts consolidation because materials will be more efficient. This material can fill the wood pores and increase the density by 13,89%. The resulting compressive strength value reached 248,01 kg/cm2 or increased by 43,18%, higher than Paraloid B72 10%. Shellac 7,5% does not change the color of the wood and safe from fungal growth when applied to wood. This material also does not change the chemical composition of wood. Keywords: wood, artifact, consolidation, shellac, gelatin, Paraloid B72

Analysis of Curing Agent on the Strength of Lightweight Soil Using Recycled Sludge

2014 ◽  
Vol 936 ◽  
pp. 1382-1386
Author(s):  
Guo Cai Wang ◽  
Lin Chun Yu ◽  
Ling Sha
Keyword(s):  
Compressive Strength ◽  
Unconfined Compressive Strength ◽  
Soft Soil ◽  
Strength Properties ◽  
Strength Test ◽  
Curing Agent ◽  
Test Results ◽  
Pore Characteristics ◽  
Optimum Proportion ◽  
Compressive Strength Test

In order to study the inorganic composite curing agents of lime, gypsum, fly ash on the strength properties of EPS lightweight soil using recycled sludge, the unconfined compressive strength test and scanning electron microscope test are done to investigate the strength properties of EPS lightweight soil. The effect and scope of each curing agent is investigated and determined by means of single-doped unconfined compressive strength test, and the optimum proportion of the curing agent is further determined by the method of orthogonal unconfined compressive strength test, of which the stabilized effectiveness of the lightweight soil is compared with those only using cement as curing agent. Finally, the SEM test is done to study the microstructure and pore characteristics of the lightweight soil mixed with EPS adding with or without curing agent. The test results and curing agent can be used as conference when stabilizing soft soil and treatment of discarded clay.

scholarly journals Pozzolanic and mechanical properties of Date Palm Seed Ash (Dpsa) concrete

2020 ◽  
Vol 39 (3) ◽  
pp. 680-686
Author(s):  
A.S.J. Smith ◽  
G. Xu ◽  
M.J. Garba ◽  
M.Y. Aliyu
Keyword(s):  
Mechanical Properties ◽  
Compressive Strength ◽  
Water Absorption ◽  
Date Palm ◽  
Activity Index ◽  
Strength Test ◽  
Partial Replacement ◽  
Test Results ◽  
Setting Times ◽  
Compressive Strength Test

This paper presents the findings of a research work conducted on how to improve the mechanical properties of concrete using Date Palm Seed Ash (DPSA) as partial replacement of cement. The DPSA used was obtained by controlled burning of date palm seed in a kiln at a maximum temperature of 630oC for eight hours and air cooled afterwards. The ash obtained was sieved through 75μm sieve and its oxide composition analysed using X-ray fluorescence (XRF) procedures. DoE method of mix design was used to produce concrete ingredients for grade 30N/mm2 giving a water-cement ratio of 0.53. The effect of partial replacement of cement with DPSA on cement paste and concrete using 0, 2.5, 5, 7.5, 10, 15 and 20% DPSA was investigated through consistency and setting times tests, workability test, compressive strength test (at 7, 21, 28 and 56 days curing duration), pozzolanic activity index evaluation and water absorption test. Results show that DPSA has high silicon dioxide (45.50%), aluminum oxide (20.75%) and Iron oxide (7.25%). Findings indicate that the consistency and setting times of cement-DPSA paste increased with increase in the replacement of cement with DPSA. The workability of DPSA concrete decreased with increase in cement replacement. Compressive strength test results show that cement can be replaced with DPSA up to 10% as the compressive strength at 10% replacement is 31.5N/mm2 as against the 31N/mm2 of the normal concrete, at 56 days. The pozzolanic activity index result also show that DPSA concrete meets up the minimum requirement of 75% specified by ASTM C618-15. Also, the water absorption capacity of DPSA concrete at the highest replacement (20%) is 11% less than that at 0%. Keywords: Cement, Compressive strength, Concrete, Date palm seed ash, Partial replacement, Pozzolana

Sign in / Sign up

Export Citation Format

Share Document