scholarly journals Numerical Simulation of Moving Heat Flux during Selective Laser Melting of AlSi25 Alloy Powder

Metals ◽  
2020 ◽  
Vol 10 (7) ◽  
pp. 877
Author(s):  
Cong Ma ◽  
Xianshun Wei ◽  
Biao Yan ◽  
Pengfei Yan
Keyword(s):  
Numerical Simulation ◽  
Selective Laser Melting ◽  
Process Parameters ◽  
Molten Pool ◽  
Laser Power ◽  
Scanning Speed ◽  
Powder Layer ◽  
Maximum Temperature ◽  
Three Dimensional Model ◽  
Laser Melting

A single-layer three-dimensional model was created to simulate multi-channel scanning of AlSi25 powder in selective laser melting (SLM) by the finite element method. Thermal behaviors of laser power and scanning speed in the procedure of SLM AlSi25 powder were studied. With the increase of laser power, the maximum temperature, size and cooling rate of the molten pool increase, while the scanning speed decreases. For an expected SLM process, a perfect molten pool can be generated using process parameters of laser power of 180 W and a scanning speed of 200 mm/s. The pool is greater than the width of the scanning interval, the depth of the molten pool is close to scan powder layer thickness, the temperature of the molten pool is higher than the melting point temperature of the powder and the parameters of the width and depth are the highest. To confirm the accuracy of the simulation results of forecasting excellent process parameters, the SLM experiment of forming AlSi25 powder was carried out. The surface morphology of the printed sample is intact without holes and defects, and a satisfactory metallurgical bond between adjacent scanning channels and adjacent scanning layers was achieved. Therefore, the development of numerical simulation in this paper provides an effective method to obtain the best process parameters, which can be used as a choice to further improve SLM process parameters. In the future, metallographic technology can also be implemented to obtain the width-to-depth ratio of the SLM sample molten pool, enhancing the connection between experiment and theory.

Effects of the Processing Parameters on the Forming Quality of Stainless Steel Parts by Selective Laser Melting

2011 ◽  
Vol 189-193 ◽  
pp. 3668-3671 ◽  
Author(s):  
Qing Song Wei ◽  
Xiao Zhao ◽  
Li Wang ◽  
Rui Di Li ◽  
Jie Liu ◽  
...  
Keyword(s):  
Layer Thickness ◽  
Selective Laser Melting ◽  
Molten Pool ◽  
Laser Power ◽  
Single Layer ◽  
Scanning Speed ◽  
Processing Parameters ◽  
Powder Layer ◽  
Laser Melting

Selective Laser Melting (SLM) can produce high-performance metal parts with complex structures. However, it’s difficult to control the processing parameters, because many factors involves. From the perspective of the molten pool, the study focuses on the effects of processing parameters, including scanning speed, laser power, scanning space, layer thickness, and scanning strategies, on the surface quality, the balling effect, the density of SLM parts, by conducting experiments of single track, single layer and block forming. The results show that the quality of the molten pool is affected by laser power and scanning speed. Scanning drove in the strategy of “jumping and turning”，a smooth surface and a less balling effect will be obtained. The thicker the powder layer is, the lower density will be obtained. The optimal parameters from series of experiments are: laser power of 98W; scanning speed of 90mm/s; scanning space of 0.07mm; layer thickness of 0.1mm; and scanning strategy of “jumping and turning”.

Effect of processing parameters on forming defects during selective laser melting of AlSi10Mg powder

2020 ◽  
Vol 26 (5) ◽  
pp. 871-879 ◽  
Author(s):  
Haihua Wu ◽  
Junfeng Li ◽  
Zhengying Wei ◽  
Pei Wei
Keyword(s):  
Selective Laser Melting ◽  
Laser Power ◽  
Scanning Speed ◽  
Processing Parameters ◽  
Argon Pressure ◽  
Powder Layer ◽  
Laser Melting ◽  
Content Type ◽  
Scan Speed ◽  
Forming Defects

Purpose To fabricate a selective laser melting (SLM)-processed AlSi10Mg part with almost full density and free of any apparent pores, this study aims to investigate the effect of ambient argon pressure and laser scanning speed on the particles splash during the AlSi10Mg powder bed laser melting. Design/methodology/approach Based on the discrete element method (DEM), a 3D model of random distribution of powder particles was established, and the 3D free surface of SLM forming process was dynamically tracked by the volume of fluid, where a Gaussian laser beam acts as the energy source melting the powder bed. Through the numerical simulation and process experimental research, the effect of the applied laser power and scanning speed on the operating laser melting temperature was studied. Findings The process stability has a fundamental role in the porosity formation, which is process-dependent. The effect of the processing conditions on the process stability and the resultant forming defects were clarified. Research limitations/implications The results shows that the pores were the main defects present in the SLM-processed AlSi10Mg sample, which decreases the densification level of the sample. Practical implications The optimal processing parameters (argon pressure of 1,000 Pa, laser power of 180 W, scan speed of 1,000 mm/s, powder layer thickness of 35 µm and hatch spacing of 50 µm ) applied during laser melting can improve the quality of selective laser melting of AlSi10Mg, Social implications It can provide a technological support for 3D printing. Originality/value Based on the analysis of the pore and balling formation mechanisms, the optimal processing parameters have been obtained, which were argon pressure of 1,000 Pa, laser power of 180 W, scan speed of 1,000 mm/s, powder layer thickness of 35 µm and hatch spacing of 50 µm. Then, a near-fully dense sample free of any apparent pores on the cross-sectional microstructure was produced by SLM, wherein the relative density of the as-built samples is larger than 97.5%.

scholarly journals Selective Laser Melting of Pre-Alloyed NiTi Powder: Single-Track Study and FE Modeling with Heat Source Calibration

Materials ◽  
2021 ◽  
Vol 14 (23) ◽  
pp. 7486
Author(s):  
Stanislav V. Chernyshikhin ◽  
Denis G. Firsov ◽  
Igor V. Shishkovsky
Keyword(s):  
Heat Source ◽  
Thermal Behavior ◽  
Selective Laser Melting ◽  
Process Parameters ◽  
Laser Power ◽  
Scanning Speed ◽  
Fe Modeling ◽  
Single Track ◽  
Laser Melting ◽  
Melt Pool

Unique functional properties such as the low stiffness, superelasticity, and biocompatibility of nickel–titanium shape-memory alloys provide many applications for such materials. Selective laser melting of NiTi enables low-cost customization of devices and the manufacturing of highly complex geometries without subsequent machining. However, the technology requires optimization of process parameters in order to guarantee high mass density and to avoid deterioration of functional properties. In this work, the melt pool geometry, surface morphology, formation mode, and thermal behavior were studied. Multiple combinations of laser power and scanning speed were used for single-track preparation from pre-alloyed NiTi powder on a nitinol substrate. The experimental results show the influence of laser power and scanning speed on the depth, width, and depth-to-width aspect ratio. Additionally, a transient 3D FE model was employed to predict thermal behavior in the melt pool for different regimes. In this paper, the coefficients for a volumetric double-ellipsoid heat source were calibrated with bound optimization by a quadratic approximation algorithm, the design of experiments technique, and experimentally obtained data. The results of the simulation reveal the necessary conditions of transition from conduction to keyhole mode welding. Finally, by combining experimental and FE modeling results, the optimal SLM process parameters were evaluated as P = 77 W, V = 400 mm/s, h = 70 μm, and t = 50 μm, without printing of 3D samples.

scholarly journals Research on the Effect of Key Technological Parameters on Molten Pool during Selective Laser Melting Processing

2021 ◽  
Vol 2097 (1) ◽  
pp. 012016
Author(s):  
Wentong Wang ◽  
Linfeng Tang ◽  
Congyan Chen ◽  
Yu Li ◽  
Tao Zhou
Keyword(s):  
Temperature Field ◽  
Selective Laser Melting ◽  
Molten Pool ◽  
Laser Power ◽  
Reference Value ◽  
Scanning Speed ◽  
Ansys Software ◽  
Technological Parameters ◽  
Laser Melting ◽  
Forming Process

Abstract Selective laser melting (SLM), as an emerging technology in additive manufacturing, often has various defects in the forming process. To ensure the consistency and stability of the parts forming quality, the effects of two typical technological parameters, laser power and scanning speed, on the temperature of molten pool are investigated in this paper. Firstly, the temperature field of Ti-6Al-4V is simulated theoretically via ANSYS software, and the effects of two typical technological parameters on the temperature field are studied. Then, in the experiment, using the designed radiation monitoring device and Ti-6Al-4V powder as forming material, the influence of these two typical factors on the state of molten pool is studied. The simulation and experimental results show that the temperature of molten pool shows positive correlation with the laser power and negative correlation with the scanning speed. This will provide a certain reference value for upgrading and optimizing SLM equipment.

scholarly journals The Influence of Selective Laser Melting Process Parameters on the Property of TiAlN/TiN Multilayer Coating on the 316L Steel

Coatings ◽  
2019 ◽  
Vol 9 (6) ◽  
pp. 377 ◽  
Author(s):  
Yueling Lyu ◽  
Jingwei Wang ◽  
Yulin Wan ◽  
Yangzhi Chen
Keyword(s):  
Selective Laser Melting ◽  
Process Parameters ◽  
Laser Power ◽  
Orthogonal Experiment ◽  
Multilayer Coating ◽  
Melting Process ◽  
Scanning Speed ◽  
Laser Melting ◽  
Wear Rates ◽  
Comprehensive Property

Selective laser melting (SLM) is an important advanced additive manufacturing technology. The existing SLM products cannot fully meet the requirements of high-precision and strength of the mechanical component because of their defects. The TiAlN/TiN multilayer coating can improve the surface property of SLM products. The present work aims to explore the influences of different process parameters of SLM on the property of TiAlN/TiN multilayer coating plating on the 361L specimen and the mechanism of these influences. Taking laser power, scanning speed, and scanning space as factors, an orthogonal experiment was designed. The TiAlN/TiN multilayer coating specimens can be obtained by plating on the 361L specimen, fabricated by the process parameters of SLM on the orthogonal experiment. The surface topographies and properties of TiAlN/TiN multilayer coating were tested, the influences of SLM process parameters on TiAlN/TiN multilayer coating were analyzed, and the optimal process parameter was obtained. The electron microscope images revealed that the surface morphology of TiAlN/TiN multilayer coating plating on the SLM specimen was relatively flat, and there were some macro-particles in different sizes and pin holes dispersed on it. The thickness of the TiAlN/TiN multilayer coating was 2.77–3.29 μm. The microhardness value of coating SLM specimen was more than four times that of the uncoated SLM specimen and the wear rates of the uncoated specimen were 2–4 times that of the corresponding coating specimen. The comprehensive analysis shows that the laser power had the greatest influence on the comprehensive property of the coating. The primary cause of the influence of SLM process parameters on the properties of the TiAlN/TiN multilayer coating was preliminarily discussed. When the laser power was 170 W, the scanning speed was 1,100 mm/s, and the scanning space was 0.08mm, the TiAlN/TiN multilayer coating plating on the SLM specimen had the best comprehensive property.

scholarly journals Mechanical Properties of High-Strength Cu–Cr–Zr Alloy Fabricated by Selective Laser Melting

Materials ◽  
2020 ◽  
Vol 13 (21) ◽  
pp. 5028
Author(s):  
Fujia Sun ◽  
Ping Liu ◽  
Xiaohong Chen ◽  
Honglei Zhou ◽  
Pengfei Guan ◽  
...  
Keyword(s):  
Tensile Strength ◽  
Selective Laser Melting ◽  
Process Parameters ◽  
Laser Power ◽  
High Efficiency ◽  
High Strength ◽  
Scanning Speed ◽  
Laser Melting ◽  
Ansys Simulation ◽  
Zr Alloy

The approximate process range for preparing the Cu–Cr–Zr alloy by selective laser melting (SLM) was determined by ANSYS simulation, and the influence of the SLM process parameters on the comprehensive properties of the SLM-formed alloy was studied by the design of experiments. The Cu–Cr–Zr alloy with optimum strength and hardness was prepared with high efficiency by optimizing the process parameters for SLM (i.e., laser power, scanning speed, and hatching distance). It is experimentally shown that tensile strength and hardness of the SLM alloy are increased by increasing laser power and decreasing scanning speed, whereas they are initially increased and then decreased by increasing the hatching distance. Moreover, strength, roughness and hardness of the SLM alloy are optimized when laser power is 460 W, scanning speed is 700 mm/s and hatching distance is 0.06 mm. The optimized properties of the SLM alloy are a tensile strength of 153.5 MPa, hardness of 119 HV, roughness of 31.384 μm and relative density of 91.62%.

scholarly journals Influence of Material Property Variation on Computationally Calculated Melt Pool Temperature during Laser Melting Process

Metals ◽  
2019 ◽  
Vol 9 (4) ◽  
pp. 456 ◽  
Author(s):  
Sazzad H. Ahmed ◽  
Ahsan Mian
Keyword(s):  
Thermal Conductivity ◽  
Specific Heat ◽  
Process Parameters ◽  
Laser Power ◽  
Laser Scanning ◽  
Peak Temperature ◽  
Powder Layer ◽  
Laser Melting ◽  
Melt Pool ◽  
Melt Pool Temperature

Selective Laser Melting (SLM) is a popular additive manufacturing (AM) method where a laser beam selectively melts powder layer by layer based on the building geometry. The melt pool peak temperature during build process is an important parameter to determine build quality of a fabricated component by SLM process. The melt pool temperature depends on process parameters including laser power, scanning speed, and hatch space as well as the properties of the build material. In this paper, the sensitivity of melt pool peak temperature during the build process to temperature dependent material properties including density, specific heat, and thermal conductivity are investigated for a range of laser powers and laser scanning speeds. It is observed that the melt pool temperature is most sensitive to melt pool thermal conductivity of the processed material for a set of specific process parameters (e.g., laser power and scan speed). Variations in the other mechanical–physical properties of powder and melt pool such as density and specific heat are found to have minimal effect on melt pool temperature.

Single Track Formation during Selective Laser Melting of Ti-6Al-4V Alloy

2019 ◽  
Vol 946 ◽  
pp. 978-983 ◽  
Author(s):  
R.M. Baitimerov
Keyword(s):  
Selective Laser Melting ◽  
Process Parameters ◽  
Complex Shape ◽  
Powder Layer ◽  
Single Track ◽  
Laser Melting ◽  
Additive Manufacturing Technology ◽  
Geometrical Characteristics ◽  
Track Formation ◽  
Point Distance

Selective laser melting (SLM) is an additive manufacturing technology that allows to produce functional parts with extremely complex shape from metal powder feedstock. 240 single tracks with the length of 10 mm were fabricated using different SLM process parameters: laser power output, powder layer thickness, point distance and exposure time. Obtained single tracks were measured using optical microscopy. An influence of SLM process parameters on geometrical characteristics of obtained single tracks was investigated.

scholarly journals The Influence of Process Parameters and Scanning Strategy on Lower Surface Quality of TA15 Parts Fabricated by Selective Laser Melting

Metals ◽  
2020 ◽  
Vol 10 (9) ◽  
pp. 1228
Author(s):  
Junjie Jiang ◽  
Jianming Chen ◽  
Zhihao Ren ◽  
Zhongfa Mao ◽  
Xiangyu Ma ◽  
...  
Keyword(s):  
Surface Quality ◽  
Selective Laser Melting ◽  
Process Parameters ◽  
Flexible Manufacturing ◽  
Molten Pool ◽  
Lower Surface ◽  
Laser Melting ◽  
Scanning Strategy ◽  
Influence Of Process Parameters

With superior flexible manufacturing capability, selective laser melting (SLM) has attracted more and more attention in the aerospace, medical, and automotive industries. However, the poor quality of the lower surface in overhanging structures is still one of the factors that limits the wide application of SLM. In this work, the influence of process parameters and scanning strategy on the lower surface quality of SLMed TA15 (Ti-6Al-2Zr-1Mo-1V) titanium alloy parts were studied. The results showed that the laser surface energy density (EF) had a significant influence on the quality of the lower surface. Excessive EF led to obvious sinking of the molten pool and a serious slag hanging phenomenon. However, the too low EF easily contributed to the insufficient powder fusion in the lower surface area, which led to the agglomeration of a molten pool during core processing, resulting in slag hanging, pores, and powder spalling that reduced the quality of the lower surface. Moreover, the cross-remelting strategy and non-remelting strategy gained better surface quality at the low EF and high EF, respectively. In addition, it was found that the quality of the lower surface could be quickly and accurately evaluated by the cooling time of the molten pool during the processing of the lower surface. This research can increase the understanding of the forming mechanism of the lower surface and has certain guiding significance for the process optimization of the lower surface.

Influence of Selective Laser Melting Process Parameters on Densification Behavior, Surface Quality and Hardness of 18Ni300 Steel

2020 ◽  
Vol 861 ◽  
pp. 77-82
Author(s):  
Gan Li ◽  
Cheng Guo ◽  
Wen Feng Guo ◽  
Hong Xing Lu ◽  
Lin Ju Wen ◽  
...  
Keyword(s):  
Energy Density ◽  
Relative Density ◽  
Maraging Steel ◽  
Surface Quality ◽  
Selective Laser Melting ◽  
Process Parameters ◽  
Laser Power ◽  
Densification Behavior ◽  
Laser Melting ◽  
Scan Speed

This study investigated the effect of laser power (P), scan speed (v) and hatch space (h) on densification behavior, surface quality and hardness of 18Ni300 maraging steel fabricated by selective laser melting (SLM). The results indicated that the relative density of the SLMed samples has a shape increase from 73% to 97% with the laser energy density increasing from 0.5 to 2.2 J/mm2. The relative density ≥ 99% was achieved at the energy density in the range of 2.2~5.9 J/mm2. The optimum process parameters were found to be laser power of 150~200 W, scan speed of 600mm/s and hatch space of 0.105mm. In addition, it was found that the hardness increased initially with the increasing relative density up to relative density of 90% and then little relationship, but finally increase again significantly. This work provides reference for determining process parameters for SLMed maraging steel and the development of 3D printing of die steels.

Sign in / Sign up

Export Citation Format

Share Document