Mangnese Dioxide Nano-Crystal as Catalyst to Remove Formaldehyde

2011 ◽  
Vol 298 ◽  
pp. 147-152 ◽  
Author(s):  
Wei Shao ◽  
Xiu Juan Chu ◽  
Kai Gao ◽  
Hua Zhang
Keyword(s):  
Hot Spot ◽  
Structure And Properties ◽  
X Ray Diffraction ◽  
X Ray ◽  
Transmission Electron ◽  
Formaldehyde Oxidation ◽  
Nano Crystal ◽  
Liquid Precipitation ◽  
Scanning Electron ◽  
Better Than

The purification technology and material of indoor formaldehyde is a hot spot in the field of material at present. In this paper, MnSO4, KMnO4, NaOH and H2O2 etc. are used to make manganese dioxide nanocrystal with the method of liquid precipitation. X-ray diffraction (XRD), scanning electron microscope (SEM) and transmission electron microscopy (TEM) were used to characterize the structure and properties. The results show that the products are nano-crystals of γ- MnO2 and δ-MnO2. The catalyze oxidation of formaldehyde using bothγ- MnO2 and δ-MnO2 as catalysts was investigated; and acetyl acetone method was used to characterize formaldehyde chroma. The catalytic ability ofγ-MnO2 nanocrystal to catalyze formaldehyde oxidation is better than that ofδ-MnO2.

The Use of Advanced Analytical Techniques for Characterization of the Chemical, Physical, and Crystallographic Nature of a Surface

1973 ◽  
Vol 31 ◽  
pp. 132-133 ◽  
Author(s):  
R. E. Herfert
Keyword(s):  
Surface Characterization ◽  
Analytical Techniques ◽  
X Ray Diffraction ◽  
Depth Of Penetration ◽  
X Ray ◽  
The Past ◽  
Transmission Electron ◽  
Scanning Electron

Studies of the nature of a surface, either metallic or nonmetallic, in the past, have been limited to the instrumentation available for these measurements. In the past, optical microscopy, replica transmission electron microscopy, electron or X-ray diffraction and optical or X-ray spectroscopy have provided the means of surface characterization. Actually, some of these techniques are not purely surface; the depth of penetration may be a few thousands of an inch. Within the last five years, instrumentation has been made available which now makes it practical for use to study the outer few 100A of layers and characterize it completely from a chemical, physical, and crystallographic standpoint. The scanning electron microscope (SEM) provides a means of viewing the surface of a material in situ to magnifications as high as 250,000X.

Identification of calcium oxalate crystals in dried or fixed tobacco leaf

1984 ◽  
Vol 42 ◽  
pp. 288-289
Author(s):  
Vicki L. Baliga ◽  
Mary Ellen Counts
Keyword(s):  
Electron Microscopy ◽  
Scanning Electron Microscopy ◽  
Calcium Oxalate ◽  
Growth And Development ◽  
Polarized Light ◽  
Calcium Oxalate Crystals ◽  
X Ray Diffraction ◽  
X Ray ◽  
Transmission Electron ◽  
Scanning Electron

Calcium is an important element in the growth and development of plants and one form of calcium is calcium oxalate. Calcium oxalate has been found in leaf seed, stem material plant tissue culture, fungi and lichen using one or more of the following methods—polarized light microscopy (PLM), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and x-ray diffraction.Two methods are presented here for qualitatively estimating calcium oxalate in dried or fixed tobacco (Nicotiana) leaf from different stalk positions using PLM. SEM, coupled with energy dispersive x-ray spectrometry (EDS), and powder x-ray diffraction were used to verify that the crystals observed in the dried leaf with PLM were calcium oxalate.

The Effect of the Microstructure of Diffusion Barriers on the Palladium Activation for Electroless Copper Deposition

2002 ◽  
Vol 716 ◽  
Author(s):  
Seok Woo Hong ◽  
Yong Sun Lee ◽  
Ki-Chul Park ◽  
Jong-Wan Park
Keyword(s):  
Electron Microscopy ◽  
Diffusion Barriers ◽  
Copper Deposition ◽  
X Ray Diffraction ◽  
Plan View ◽  
X Ray ◽  
Transmission Electron ◽  
Electroless Copper ◽  
Sheet Resistance Measurement ◽  
Scanning Electron

AbstractThe effect of microstructure of dc magnetron sputtered TiN and TaN diffusion barriers on the palladium activation for autocatalytic electroless copper deposition has been investigated by using X-ray diffraction, sheet resistance measurement, field emission scanning electron microscopy (FE-SEM) and plan view transmission electron microscopy (TEM). The density of palladium nuclei on TaN diffusion barrier increases as the grain size of TaN films decreases, which was caused by increasing nitrogen content in TaN films. Plan view TEM results of TiN and TaN diffusiton barriers showed that palladium nuclei formed mainly on the grain boundaries of the diffusion barriers.

Hydrothermal Synthesis and Characterization of BiFeO3 Polyhedral Crystallites

2012 ◽  
Vol 174-177 ◽  
pp. 508-511
Author(s):  
Lin Lin Yang ◽  
Yong Gang Wang ◽  
Yu Jiang Wang ◽  
Xiao Feng Wang
Keyword(s):  
Electron Microscopy ◽  
Scanning Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
Synthesis And Characterization ◽  
X Ray Diffraction ◽  
Xrd Pattern ◽  
X Ray ◽  
Transmission Electron ◽  
Scanning Electron

BiFeO3 polyhedrons had been successfully synthesized via a hydrothermal method. The as-prepared products were characterized by power X-ray diffraction (XRD) pattern, scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The possible mechanisms for the formation of BiFeO3 polyhedrons were discussed. Though comparison experiments, it was found that the kind of precursor played a key role on the morphology control of BiFeO3 crystals.

Solvothermal Synthesis of Bi2Se3 Hexagonal Nanosheet Crystals

2011 ◽  
Vol 236-238 ◽  
pp. 1712-1716 ◽  
Author(s):  
Hai Tao Liu ◽  
Jun Dai ◽  
Jia Jia Zhang ◽  
Wei Dong Xiang
Keyword(s):  
Electron Microscope ◽  
Solvothermal Synthesis ◽  
Solvothermal Method ◽  
Raw Materials ◽  
X Ray Diffraction ◽  
Uniform Size ◽  
X Ray ◽  
Selected Area Electron Diffraction ◽  
Transmission Electron ◽  
Scanning Electron

Bismuth selenide (Bi2Se3) hexagonal nanosheet crystals with uniform size were successfully prepared via a solvothermal method at 160°C for 22 h using bismuth trichloride(BiCl3) and selenium powder(Se) as raw materials, sodium bisulfite(NaHSO3) as a reducing agent, diethylene glycol(DEG) as solvent, and ammonia as pH regulator. Various techniques such as X-ray diffraction (XRD), field-emission scanning electron microscope (FESEM), high-resolution transmission electron microscope (HRTEM), and selected area electron diffraction (SAED) were used to characterize the obtained products. Results show that the as-synthesized samples are pure Bi2Se3 hexagonal nanosheet crystals. A possible growth mechanism for Bi2Se3 hexagonal nanosheet crystals is also discussed based on the experiment.

Synthesis and Study the Properties of a Solar Cell of Gold Nanoparticles Prepared in a Simple Chemical Way

2021 ◽  
Vol 19 (11) ◽  
pp. 66-71
Author(s):  
Maithm A. Obaid ◽  
Suha A Fadaam ◽  
Osama S. Hashim
Keyword(s):  
Electron Microscopy ◽  
Gold Nanoparticles ◽  
Chemical Method ◽  
X Ray Diffraction ◽  
Structural And Optical Properties ◽  
Casting Method ◽  
X Ray ◽  
Transmission Electron ◽  
Simple Chemical ◽  
Scanning Electron

The aim of this study is to prepare gold nanoparticles by a simple chemical method at a temperature of 70°C. The solution was dried on glass basest by Casting method, the rate of five drops per sample At a temperature 100 C. Then the structural and optical properties have been confirmed by X-ray diffraction, scanning electron microscopy (SEM) and Transmission Electron microscope (TEM), Fourier Transform Infrared Spectroscopy (FTIR) and spectrum.

scholarly journals Chemical Stability of Ti3C2 MXene with Al in the Temperature Range 500–700 °C

Materials ◽  
2018 ◽  
Vol 11 (10) ◽  
pp. 1979 ◽  
Author(s):  
Jing Zhang ◽  
Shibo Li ◽  
Shujun Hu ◽  
Yang Zhou
Keyword(s):  
Electron Microscopy ◽  
Chemical Stability ◽  
Metal Matrix ◽  
Matrix Composites ◽  
X Ray Diffraction ◽  
X Ray ◽  
Temperature Range ◽  
Transmission Electron ◽  
Work First ◽  
Scanning Electron

Ti3C2Tx MXene, a new 2D nanosheet material, is expected to be an attractive reinforcement of metal matrix composites because its surfaces are terminated with Ti and/or functional groups of –OH, –O, and –F which improve its wettability with metals. Thus, new Ti3C2Tx/Al composites with strong interfaces and novel properties are desired. To prepare such composites, the chemical stability of Ti3C2Tx with Al at high temperatures should be investigated. This work first reports on the chemical stability of Ti3C2Tx MXene with Al in the temperature range 500–700 °C. Ti3C2Tx is thermally stable with Al at temperatures below 700 °C, but it reacts with Al to form Al3Ti and TiC at temperatures above 700 °C. The chemical stability and microstructure of the Ti3C2Tx/Al samples were investigated by differential scanning calorimeter, X-ray diffraction analysis, scanning electron microscopy, and transmission electron microscopy.

Influence of Salt Aid on Combustion Synthesis of Nanocrystalline CeO2 Powders

2011 ◽  
Vol 412 ◽  
pp. 5-8 ◽  
Author(s):  
Ying Zhang ◽  
Ai Chen ◽  
Hai Rong Wang ◽  
Ze Song Li ◽  
Ying Ping Shen
Keyword(s):  
Electron Microscopy ◽  
Scanning Electron Microscopy ◽  
Transmission Electron Microscopy ◽  
Combustion Process ◽  
X Ray Diffraction ◽  
X Ray ◽  
Particle Characteristics ◽  
Transmission Electron ◽  
Nanocrystalline Ceria ◽  
Scanning Electron

The present article reports the results of studies related to the synthesis of nanocrystalline ceria powder by combustion process using salt combustion aid. Cerium nitrate as oxidant and urea as fuel were used as reagents, Sodium Chloride was compared as combustion aid. The phase analysis and particle size were compared. The product was characterized by X-ray diffraction, Scanning electron microscopy and Transmission electron microscopy. The results showed that employment of starting fuel with combustion aid resulted in synthesizing nanocrystalline ceria powder with fine agglomerates. By using combustion aid, the energetics of the combustion reaction and particle characteristics have been changed.

scholarly journals Mechanical Activation of Smectite-Based Nanocomposites for Creation of Smart Fertilizers

2022 ◽  
Vol 12 (2) ◽  
pp. 809
Author(s):  
Maxim Rudmin ◽  
Santanu Banerjee ◽  
Boris Makarov ◽  
Kanipa Ibraeva ◽  
Alexander Konstantinov
Keyword(s):  
Electron Microscopy ◽  
Interlayer Space ◽  
Soil Leaching ◽  
X Ray Diffraction ◽  
Activation Time ◽  
Release Rates ◽  
X Ray ◽  
Weight Losses ◽  
Transmission Electron ◽  
Scanning Electron

This research presents the mechanical creation of smart fertilizers from a mixture of smectite and urea in a 3:2 ratio by using the planetary milling technique. The smectite–urea composites show intercalation between urea and mineral, which increases steadily with increasing activation time. A shift of X-Ray Diffraction basal reflections, intensities of Fourier transform infrared spectroscopy (FTIR) peaks, and weight losses in thermogravimetric analysis (TG) document the systematic crystallo-chemical changes of the composites related to nitrogen interaction with activation. Observations of the nanocomposites by scanning electron microscopy (SEM) and transmission electron microscopy (TEM) corroborate the inference. Nitrogen intercalates with smectite in the interlayer space and remains absorbed either within micro-aggregates or on the surface of activated smectites. Soil leaching tests reveal a slower rate of nitrogen than that of traditional urea fertilizers. Different forms of nitrogen within the composites cause their differential release rates to the soil. The formulated nanocomposite fertilizer enhances the quality and quantity of oat yield.

Synthesis and characterization of homogeneous lead-substituted tin oxide with the (110) face of rutile structure

2000 ◽  
Vol 15 (10) ◽  
pp. 2076-2079
Author(s):  
Chika Nozaki ◽  
Takashi Yamada ◽  
Kenji Tabata ◽  
Eiji Suzuki
Keyword(s):  
Electron Microscopy ◽  
Tin Oxide ◽  
Photoelectron Spectroscopy ◽  
Synthesis And Characterization ◽  
X Ray Diffraction ◽  
Rutile Structure ◽  
X Ray ◽  
Transmission Electron ◽  
Scanning Electron

Synthesis of a rutile-type lead-substituted tin oxide with (110) face was investigated. The characterization was performed by x-ray diffraction, scanning electron microscopy, transmission electron microscopy, energy dispersive x-ray spectroscopy, infrared spectroscopy, x-ray photoelectron spectroscopy, and Brunauer–Emmett–Teller surface area measurements. The homogeneous rutile-type lead-substituted tin oxide was obtained until 4.1 mol% of tin was substituted with lead. The surface of obtained oxide had a homogeneously lead-substituted (110) face.

Sign in / Sign up

Export Citation Format

Share Document