Effect of Enamel Pretreatment with Pastes Presenting Different Relative Dentin Abrasivity (RDA) Values on Orthodontic Bracket Bonding Efficacy of Microfilled Composite Resin: In Vitro Investigation and Randomized Clinical Trial

Bonding failure is a clinical issue frequently encountered in orthodontic practice. The aim of this study was to evaluate enamel pretreatment both in vitro and clinically using agents with different RDA values before brackets’ bonding, to assess if RDA can affect the Shear Bond Strength (SBS), Adhesive Remnant Index (ARI) and clinical failure rate of orthodontic brackets. For the in vitro study, 220 bovine teeth were pretreated with agents with different RDA values. Subsequently, brackets were bonded. For the clinical study, 20 patients underwent bonding of 20 brackets each with a split-mouth design. Low and high RDA toothpastes were used for enamel pretreatment. SBS, ARI and failures were recorded. Higher SBS values were found for teeth pretreated with lower RDA agents; conversely, lower SBS values were found for teeth pretreated with higher RDA agents (p < 0.05). For high ARI values, RDA increased too (p > 0.05). In the clinical study, a significantly lower failure rate was reported for teeth pretreated with low RDA toothpaste (2.5% in low RDA group, 7.0% in high RDA group; p < 0.05). No significant differences were assessed comparing the two dental arches and anterior and posterior sites. Enamel pretreatment with low RDA toothpastes could increase brackets’ survival rate. Further in vitro and clinical studies would be welcomed to confirm these findings.

Effect of Thermocycling on the Bond Strength of Self-Adhesive Resin Cements Used for Luting CAD/CAM Ceramics to Human Dentin

The aim of the study was to evaluate the influence of thermocycling on the shear bond strength of self-adhesive, self-etching resin cements luted to human dentin and computer-aided design/computer-aided manufacturing (CAD/CAM) ceramics. Three modern self-adhesive dental cements (Maxcem Elite, RelyX U200, Panavia SA) were used to lute three CAD/CAM ceramics (IPS Empress CAD, IPS e.max CAD, IPS e.max ZirCAD) onto the dentin. One conventional cement (Panavia V5) served as a control. After preparation, the samples were subjected to thermocycling as a method of artificial aging of dental materials applied to simulate long-term use in oral conditions. Shear bond strength was evaluated according to PN-EN ISO 29022:2013-10 and failure modes were observed under a light microscope. Statistical analysis was performed. The study demonstrated that a combination of ceramics and cements directly impacts the bond strength. The highest bond strength was observed in Panavia V5, lower in Panavia SA and Maxcem Elite and the lowest–in RelyX U200. Adhesive failure between human dentin and cements was the most common failure mode. Moreover, thermocycling highly decreased bond strength of self-adhesive, self-etching cements.

Influence of Enamel Exposure to Acidic Drink on Shear Bond Strength of Different Fissure Sealants

In the present study, we evaluated the influence of bovine enamel exposure to acidic drinks (Coca-Cola, Coca-Cola Company, Milano, Italy, pH = 2.37) on shear bond strength of three sealants (Fissurit; Grandio Seal and Admira Fusion—Voco Gmbh, Cuxhaven, Germany). For each sealant, two adhesive techniques were tested to investigate the impact of the adhesive application on shear bond strength of sealants after immersion in acidic drink and in the control: Group 1—Control: enamel surface was not in contact with acid drinks, acid etching application and self-adhesive technique for fissure sealant; Group 2—enamel surface was not in contact with acid drinks, acid etching, and adhesive applications, an etch-and-rinse technique for fissure sealant; Group 3—enamel surface was immersed in acid drink, acid etching application and self-adhesive technique for fissure sealant; Group 4—enamel surface was immersed in acid drink, acid etching, and adhesive applications, an etch-and-rinse technique for fissure sealant. For each specimen, the sealant composite resin was applied to the enamel surface and tested with a universal testing machine. Shear bond strength was measured in MPa and with an optical microscope to determine failure modes, quantified with adhesive remnant index (ARI). Enamel acidification variably influenced bond strength values of the different sealants. When no enamel pretreatment was applied, no significant differences were found among the sealants (p > 0.05). However, the mere application of acid etching without adhesive procedures resulted in lower bond strength (p < 0.001). The acid pretreatment affected significantly the bond strength of all sealants tested (p < 0.001), but no significant differences were recorded between the subgroups.

Shear bond strength of ceramic laminate veneers to finishing surfaces with different percentages of preserved enamel under a digital guided method

Background The purpose of this in vitro study was to evaluate the effect of the percentages of preserved enamel on ceramic laminate veneers’ (CLVs) shear bond strength (SBS). Methods Seventy extracted human maxillary central incisors were scanned and reconstructed into three-dimensional models. The extracted teeth were then embedded and randomly divided into seven groups (n = 10 per group). Based on digital analyses of the three-dimensional models, guided tooth preparation and bonding procedures were performed individually to form seven different percentages (100%, 80%, 60% 50%, 40%, 20% and 0%) of remaining enamel thickness on the bonding surface. Finally, the SBS test was performed, and the data were statistically analysed by one-way ANOVA with LSD post hoc test (α = 0.05). Results The complete enamel surface exhibited the highest SBS (19.93 ± 4.55 MPa), followed by 80% enamel (19.03 ± 3.66 MPa), 60% enamel (18.44 ± 3.65 MPa), 50% enamel (18.18 ± 3.41 MPa), 40% enamel (17.83 ± 3.01 MPa) and 20% enamel (11.32 ± 3.42 MPa) group. The lowest SBS (9.63 ± 3.46 MPa) was detected in 0% enamel group. No significant difference was observed among the 40–100% enamel groups, while the 20% or 0% enamel group demonstrated a significantly lower mean SBS than the 40% enamel group (p < 0.05). Conclusion The SBS value of CLVs bonded to 100% enamel on the finishing surfaces (nearly 20 MPa) was twice that which bonded to 0% enamel (nearly 10 MPa). Bonding to 100% enamel is the most reliable treatment. When dentin exposure is inevitable, enamel should be preserved as much as possible to maintain good bonding. In addition, 40% of preserved enamel on the bonding surface was the minimal acceptable value to fulfil the requirements of good bonding strength.