PLASMA COATING FORMATION BY THE DEPOSITION OF CATHODE MATERIAL ERODED THROUGH HIGH-CURRENT PULSED DISCHARGE

The paper analyzes the conditions for the formation of a coating obtained using an electrothermal axial plasma accelerator due to plasma transfer of cathode erosion products. It is shown that by using a cathode of low-melting materials with a high-current pulsed discharge, microdrops are formed and injected from the accelerator falling into the surface to be treated. When colliding with the surface, the drops acquire near-disk shape with a radius of up to 100 μm, cooling on the substrate at a speed of up to 108 K/s. This leads to the formation in the drops of a supersatu-rated solid solution with nonequilibrium structure. The subsequent heat treatment of the coating can result in harden-ing phases precipitation from solid solution causing the increase in coating microhardness.

Molecular Dynamics Study of Nonequilibrium [112] Tilt Grain Boundaries in Ni and their Relaxation under Cyclic Deformation

Atomic structure of nonequilibrium [112] tilt grain boundaries in nickel containing disclination dipoles is studied by means of molecular dynamics simulations. Initial systems for simulations are constructed by joining together pieces of two bicrystals one of which contains a symmetric tilt GB S=11 / 62.96° and the other a GB S=105 / 57.12°, or S=125 / 55.39°, or S=31 / 52.20°, so disclination dipoles with strengths w = 5.84°, 7.58° and 10.76° are created. Stress maps plotted after relaxation at zero temperature indicate the presence of high long-range stresses induced by disclination dipoles. Excess energy of GBs due to the nonequilibrium structure is calculated. Effect of oscillating tension-compression stresses on the nonequilibrium GB structure is studied at temperature T = 300 K. The simulations show that the oscillating stress results in a generation of partial lattice dislocations by the GB, their glide across grains and sink at appropriate surfaces that results in a compensation of the disclination stress fields and recovery of an equilibrium GB structure and energy.