Influence of Defects to Zr65Cu18Ni7Al10 Bulk Metallic Glass Properties Under Dynamic Compression

The Zr65Cu18Ni7Al10 bulk metallic glass with smaller diameter exhibits higher fracture strength under dynamic compression, which is ascribed to concentration of flow defect. The density of shear bands in the sample surface will increase with decreasing of the diameter, whereas, average distance and width of tear ridges in the fracture surface will increase with larger diameter. In addition, the volume of shear transformation zone can be estimated, which presents a ductile-to-brittle transition with the change of diameter. The physical graph of shear transformation zone can be obtained from the experimental analysis.

A chronology of subterranean clover burr detachment mechanics and implications for seed harvestability

Seed retention has not been evaluated for subterranean clover ( Trifolium subterraneum L.), because its geocarpic seed-bearing burrs are currently harvested by suction systems. Development of improved harvest methods requires knowledge of subterranean clover seed retention characteristics and their changes with plant development. This study evaluates burr attachment and peduncle tensile strength during burr maturity until plant senescence across the three subspecies: subterraneum (cv. Dalkeith), yanninicum (cv. Monti) and brachycalycinum (cv. Mawson). Peduncle tensile strength was greater than burr-to-peduncle attachment strength for each subspecies, with peak mean peduncle strength 30–130% greater than peak mean burr-to-peduncle attachment strength. Both strength measurements decreased significantly (greater than 50% for each subspecies) as the plant senesced, which was associated with reductions in burr moisture content, and burr and peduncle diameters. Microscopy indicated a ductile to brittle transition as peduncles senesced, reducing energy absorption and increasing the likelihood of failure at defects. These results are important for the commercial production of subterranean clover seed and suggest it may be possible to harvest seed before plant senescence with dig-invert machinery, similar to that used for peanut harvesting. However, this approach would require harvesting prior to maximum seed development and the implications for seed viability and yield need to be further evaluated.

Elucidating the Effect of Step Cooling Heat Treatment on the Properties of 2.25 Cr–1.0 Mo Steel Welded with a Combination of GMAW Techniques Incorporating Metal-Cored Wires

The prospect of using metal-cored wires instead of solid wires during gas metal arc welding (GMAW) of 2.25 Cr–1.0 Mo steels embraces several challenges. The in-service requirements for the equipment made up of these steels are stringent. The major challenge faced by the manufacturers is temper embrittlement. In the current study, the temper embrittlement susceptibility of the welded joint was ascertained by subjecting it to step cooling heat treatment. A 25 mm thick 2.25 Cr–1.0 Mo weld joint was prepared using a combination of the regulated metal deposition (RMD) and GMAW processes incorporating metal-cored wires. After welding the plates were exposed to post-weld heat treatment followed by a rigorous step cooling heat treatment prescribed by API standards. The temper embrittlement susceptibility of the weld joint was ascertained by Bruscato X-factor as well as by formulating ductile-to-brittle transition temperature (DBTT) curves by carrying out the impact toughness testing at various temperatures. Detailed microscopy and hardness studies were also carried out. It was established from the study that the X-factor value for the welded joint was 15.4. The DBTT for the weld joint was found to occur at −37 °C which was well below 10 °C. Optical microscopy and scanning electron microscopy indicated the presence of carbides and the energy dispersive X-ray spectrometry studies indicated the presence of chromium and manganese-rich carbides along with the presence of sulfur near the grain boundaries. This study establishes a base for the usage of metal-cored wires particularly in high temperature and pressure application of Cr–Mo steels.