Physical and Mechanical Properties of Tenun Pahang Fabrics using Alternative Yarns

2016 ◽  
Vol 13 (2) ◽  
pp. 67
Author(s):  
Engku Liyana Zafirah Engku Mohd Suhaimi ◽  
Jamil Salleh ◽  
Suzaini Abd Ghani ◽  
Mohamad Faizul Yahya ◽  
Mohd Rozi Ahmad

An investigation on the properties of Tenun Pahang fabric performances using alternative yarns was conducted. The studies were made in order to evaluate whether the Tenun Pahang fabric could be produced economically and at the same time maintain the fabric quality. Traditional Tenun Pahang fabric uses silk for both warp and weft. For this project, two alternative yarns were used which were bamboo and modal, which were a little lower in cost compared to silk. These yarns were woven with two variations, one with the yarns as weft only while maintaining the silk warp and the other with both warp and weft using the alternative yarns. Four (4) physical testings and three (3) mechanical testings conducted on the fabric samples. The fabric samples were evaluated including weight, thickness, thread density, crease recovery angle, stiffness and drapability. The results show that modal/silk and bamboo silk fabrics are comparable in terms of stiffness and drapability, hence they have the potential to replace 100% silk Tenun Pahang.

2016 ◽  
Vol 13 (2) ◽  
pp. 67
Author(s):  
Engku Liyana Zafirah Engku Mohd Suhaimi ◽  
Jamil Salleh ◽  
Suzaini Abd Ghani ◽  
Mohamad Faizul Yahya ◽  
Mohd Rozi Ahmad

An investigation on the properties of Tenun Pahang fabric performances using alternative yarns was conducted. The studies were made in order to evaluate whether the Tenun Pahang fabric could be produced economically and at the same time maintain the fabric quality. Traditional Tenun Pahang fabric uses silk for both warp and weft. For this project, two alternative yarns were used which were bamboo and modal, which were a little lower in cost compared to silk. These yarns were woven with two variations, one with the yarns as weft only while maintaining the silk warp and the other with both warp and weft using the alternative yarns. Four (4) physical testings and three (3) mechanical testings conducted on the fabric samples. The fabric samples were evaluated including weight, thickness, thread density, crease recovery angle, stiffness and drapability. The results show that modal/silk and bamboo silk fabrics are comparable in terms of stiffness and drapability, hence they have the potential to replace 100% silk Tenun Pahang.


2017 ◽  
Vol 41 (1) ◽  
Author(s):  
Mírian de Almeida Costa ◽  
Cláudio Henrique Soares Del Menezzi

ABSTRACT Thermo-mechanical treatment is a technique for wood modification in which samples are densified by means of heat and mechanical compression, applied perpendicularly to fibers, which under different combinations of time, temperature, and pressure increases wood density and thus improve some of its properties. This study aimed to treat thermo-mechanically parica plywood and observe the effects on its physical and mechanical properties. Specimens were submitted to two treatments, 120 and 150 ºC, remaining under pressure for seven minutes and, subsequently, under zero pressure for 15 minutes. Results showed a significant increase in specific mass from 0.48 g cm-3 to an average of 0.56 g cm-3, and a compression ratio of about 31.7% on average. Physical properties also varied significantly and results showed that treated samples swelled and absorbed more water than those untreated, leading to a greater thickness non-return rate. This indicates the proposed thermal treatments did not release the internal compressive stress generated during panel pressing, not improving its dimensional stability as a result. On the other hand, mechanical properties were positively affected, leading to an increase of 27.5% and 51.8% in modulus of rupture after treatments at 120 and 150 ºC, respectively. Modulus of elasticity and glue-line shear strength did not vary statistically and Janka hardness was 29.7% higher after treatment at 150 ºC.


2011 ◽  
Vol 331 ◽  
pp. 270-274 ◽  
Author(s):  
Yan Yan Chu ◽  
Qing Wang ◽  
Shi Zhong Cui

Abstract:Pure TiO2 water sol, pure ZnO water sol and three compound TiO2/ZnO water sols are prepared under low temperature. Then the padding and baking process is used to put the functional sol liquid on the fabric. SEM is use to analyzed the change of surface feature and the result show that all of the water sol except pure ZnO water sol liquid formed a thin film on the fiber The stability of pure ZnO water sol is the best one and the pure TiO2 water sol is the worst one at temperature of 15°C. The compound water sols stabilities are between these two water sols and with the more amount of ZnO, the stability last longer. Both mole of TiO2 and ZnO with the rate of 5 to 5 and 7 to 3 display the best antistatic behavior, but the washing fastnesses are not good. After treatment, the moisture regain displays most dramatically changes; the next one is whiteness of fabric, but the other physical and mechanical properties have a little change.


2020 ◽  
Vol 1010 ◽  
pp. 194-199
Author(s):  
Hamdan Yahya ◽  
Aspaniza Ahmad ◽  
Ismail Ibrahim

The effect of Al2O3 to the properties of whiteware porcelain such as water absorption, bulk density, flexural strength and crystalline phases were studied systematically. The result shows that the addition of alumina at maximum 5 wt.% in porcelain bodies increased the flexural strength of the fired bodies which can reach 55.5 MPa, 30% higher than 0.0% alumina content. However, slight decrease in the other physical and mechanical properties was observed with Al2O3 addition higher than 5 wt.%, which is believed to be due to increased corundum phase compared to mullite phase in porcelain body.


2012 ◽  
Vol 727-728 ◽  
pp. 993-998 ◽  
Author(s):  
A.M.F.D. Silva ◽  
L.S. Lovise ◽  
Sérgio Neves Monteiro ◽  
Carlos Maurício Fontes Vieira

Ashes generated in industrial processes are usually discarded and contribute to environmental pollution. Large scale incorporation into clayey ceramic products for civil construction, such as bricks and tiles, could be a permanent solution. Based on this rationale, this works has as its objective to characterize an ash waste from the incineration of elephant grass and to evaluate its incorporation into a clay to produce red ceramic. The waste was submitted to mineralogical and chemical characterization. Compositions were prepared with incorporation of the waste in amounts of up to 20 wt.% into the clay. Specimens were prepared by extrusion and fired in a laboratory furnace at 850°C. The physical and mechanical properties evaluated were: linear shrinkage, water absorption and flexural strength. The results showed that the waste is mainly composed of quartz and calcium compounds that sensibly reduce the linear shrinkage and does not change the other properties of the ceramic.


Author(s):  
Adel H. Bahnasawy

The physical parameter results showed that the garlic geometric and arithmetic mean diameters ranged from 2.53 to 4.93, and 2.53 to 5.02 cm, respectively according to the bulb size categories. The cloves' length, width and thickness were 1.92 to 2.91, 0.78 to 1.32, and 0.69 to 0.99 cm, respectively. The surface and cross-sectional of areas ranged from 53.31 to 136.4 and 29.1 to 128.4 cm2, respectively. The number of cloves ranged from 18 to 51/bulb according to the bulbs size categories. Bulk density, repose angle and coefficient of contact surface values ranged from 892 to 1007 kg/m3, 41.52 to 45.04º, and 0.91 to 1.12, respectively, according to the bulb size categories.The chemical properties showed that the emptying (friction) angle ranged from 23.25 to 28.82º, where small bulbs recorded the highest values on the concrete surfaces, while the lowest values were recorded by the large bulbs on the iron surfaces. The friction coefficient decreased with increasing bulb size, where it was the highest (0.8) for the small bulbs on the concrete surfaces; on the other hand, the lowest values (0.36) were recorded for the large bulbs on the iron surfaces. The crushing load of the cloves ranged from 55.6 to 155.0 N, depending on the bulb size. The force required for loosening the cloves from the bulb ranged from 110 to 272 and 101 to 320 N on the horizontal and vertical positions of the bulbs.


2021 ◽  
Vol 891 (1) ◽  
pp. 012007
Author(s):  
Y S Hadi ◽  
E N Herliyana ◽  
I M Sulastiningsih ◽  
E Basri ◽  
R Pari ◽  
...  

Abstract Jabon (Anthocephalus cadamba) laminas were impregnated with polystyrene and reached 21.2% polymer loading. The laminas were manufactured for three-layer glued laminated timber (glulam) using isocyanate glue with glue spread 280 g/m2 and cold-press process. For comparison purposes, untreated glulam as control and also solid wood were prepared. The physical-mechanical properties were evaluated according to the Japanese Agricultural Standard (JAS) 234-2003. The results showed that the color of glulam was not different from polystyrene glulam. The density of polystyrene glulam was higher than untreated glulam and solid wood, but the moisture content was lower than the other. The product kinds of solid wood, untreated glulam, and polystyrene glulam did not affect shear strength and modulus of rupture (MOR), while the modulus of elasticity (MOE) of untreated glulam and hardness of polystyrene glulam were the highest values and the other products were not different one each other. Both kinds of glulam fulfilled the Japanese standard in terms of moisture content, MOR, and delamination in hot water, but MOE and shear strength did not. Regarding its advantages, polystyrene glulam could be further developed using a higher wood density.


2018 ◽  
Vol 27 (3) ◽  
pp. 348-354 ◽  
Author(s):  
Jakub Jura ◽  
Małgorzata Ulewicz

The article presents the results of research aimed at using glass waste and ash from biomass. The tests were carried out for cement mortars samples with using glass cullet, ash from biomass and using both wastes in 50/50 proportions. The physical and mechanical properties of the standard mortar and modified mortars were tested. Standard mortar and cement mortar samples were made in which 10, 20 and 30% of the cement mass was used as part of the standard sand. The samples were made of CEM I 42.5R. Mortars containing fly ash addition had an increased compressive strength and a smaller drop in compressive strength after frost resistance tests than standard mortar. The use of glass cullet in the amount of up to 20% did not reveal any changes in the mechanical properties of mortars, but using them in a larger amount resulted in unfavorable results. The use of a mixture of these two waste materials did not improve the results. The research has shown the possibility of using this waste to modify cement mortars.


2004 ◽  
pp. 1-6

Abstract This chapter first introduces the various factors that may alter the physical and mechanical properties of aluminum castings that are addressed in the other chapters in the book. Then, it presents the historical development of aluminum castings, followed by a discussion on the advantages and limitations of aluminum castings. Next, the chapter describes the major trends that are influencing the increased use of aluminum castings. Finally, it introduces the considerations involved in the selection of an appropriate aluminum alloy and casting process for a given application.


1956 ◽  
Vol 4 (3) ◽  
pp. 216 ◽  
Author(s):  
LD Pryor ◽  
MM Chattaway ◽  
NH Kloot

Hybrids from segregating hybrid swarms have been examined in relation to the parents. Two series of hybrids were chosen, one derived from the combination E. robertsoni x E. rossii, of the group Renantherae, and the other from E. elaeophora x E. maculosa of the group Macrantherae-Normales. The hybrids and parents were assessed according to various physical and mechanical properties of the wood, features of bark structure, field characters, and measurements of characters in the progeny raised from each. The properties of the hybrids were found to be either not significantly different from those of either parent or intermediate between those of the two parents. The degree to which they approached either parent in the various phenotypic characters examined was found, in the few cases where data were adequate, to be correlated closely with the genotype and likewise with its position in the range between the two parents. The graded sequence of variation in the characters of the different individuals in the hybrid combinations suggests those characters examined are, in general, under multiple factor control. It is likely that most Eucalyptus hybrids are intermediate as a, rule in their characters between the parents, and this applies to wood and bark characters as well as general morphological features.