Utilization of Fly Ash in High Performance Floor Screed Based on Cement and its Influence on Physical Mechanical Properties

2016 ◽  
Vol 865 ◽  
pp. 201-205 ◽  
Author(s):  
Michaela Fiedlerová ◽  
Rostislav Drochytka ◽  
Pavel Dohnálek
Keyword(s):  
Mechanical Properties ◽  
Compressive Strength ◽  
Fly Ash ◽  
Water Absorption ◽  
Bulk Density ◽  
High Performance ◽  
Power Plants ◽  
High Strength ◽  
Partial Replacement ◽  
Reference Samples

This paper deals with the evaluation of a partial replacement of cement by Czech fly ash in high strength floor screed in dosage of 10, 20, 30 and 40% and the assessment of the physical-mechanical properties such as compressive strength, water absorption and bulk density. Used fly ashes are from power plants Počerady, Opatovice and Tušimice. The experimental study showed that the use of Czech fly ash improves the compressive strength. The bulk density decreases and therefore water absorption increases. Reference samples become clearly the lowest compressive strength at age of 28 days (fc28). A significant increase in compressive strength (fc28) was observed in case of mix design with addition of 10% and 20% of fly ash Tušimice (10%ETU, 20%ETU) and 20% and 30% of fly ash Počerady (20%EPC, 30%EPC). The addition of 20% of fly ash Počerady (20%EPC) has noticeable influence on short-term compressive strength (measured at the age of 24 hours).

scholarly journals Physical and Mechanical Properties of a Porous Material Obtained by Low Replacement of Volcanic Ash by Aluminum Beverage Cans

2021 ◽  
pp. 1-11
Author(s):  
Bernard Missota Priso Dickson ◽  
Claudine Mawe Noussi ◽  
Louise Ndongo Ebongue ◽  
Joseph Dika Manga
Keyword(s):  
Mechanical Properties ◽  
Compressive Strength ◽  
Porous Material ◽  
Water Absorption ◽  
Bulk Density ◽  
Volcanic Ash ◽  
Physical And Mechanical Properties ◽  
Apparent Porosity ◽  
Partial Replacement ◽  
Inorganic Polymers

This study focuses on the evaluation of the physical and mechanical properties of a porous material based on a mixture of powder (Volcanic ash /Aluminum Beverage Cans) and a solution of phosphoric acid. Volcanic ash (VA) use was collected in one of the quarries of Mandjo (Cameroon coastal region), crushed, then characterized by XRF, DRX, FTIR and named MaJ. The various polymers obtained are called MaJ0, MaJ2.5, MaJ5, MaJ7.5 and MaJ10 according to the mass content of the additions of the powder from the aluminum beverage cans (ABCs). The physical and mechanical properties of the synthetic products were evaluated by determining the apparent porosity, bulk density, water absorption and compressive strength. The results of this study show that the partial replacement of the powder of VA by that of ABC leads to a reduction in the compressive strength (5.9 - 0.8 MPa) and bulk density (2.56 – 1.32 g/cm3) of the polymers obtained. On the other hand, apparent porosity, water absorption and pore formation within the polymers increases with addition of the powder from the beverage cans. All of these results allow us to agree that the ABCs powder can be used as a blowing agent during the synthesis of phosphate inorganic polymers.

scholarly journals INFLUENCE OF PEAT WATER ON MECHANICAL PROPERTIES OF COCONUT SHELL AND FLY ASH BASED CONCRETE

2019 ◽  
Vol 7 (2) ◽  
pp. 102-108
Author(s):  
Yulin Patrisia ◽  
Topan Eka Putra
Keyword(s):  
Mechanical Properties ◽  
Compressive Strength ◽  
Fly Ash ◽  
Water Absorption ◽  
Raw Material ◽  
Coconut Shell ◽  
Partial Replacement ◽  
Plain Water ◽  
Fine Aggregate ◽  
Coconut Shells

This study aimed to determine the influence of peat water on the mechanical properties of the paving block (compressive strength and water absorption) using coconut shell waste and fly ash as raw material. The background of the research were the lack utilization of fly ash, preparation for the handling and utilization of fly ash from power station at Pulang Pisau and Tumbang Kajuei (under construction), and the utilization of coconut shell to be more effective and economical. Paving block specimens were immersed in peat water to determine the effect of peat water and the rest were immersed in plain water. This experiment used fly ash as a partial replacement of cement and 2% coconut shell as a partial replacement of fine aggregate. The results of the analysis showed that: (a) Paving block using fly ash and coconut shells which were immersed in plain water experienced the increase in compressive strength and the decrease in water; (b) Paving block using fly ash and coconut shells soaked in peat water showed that by the increase of age, compressive strength was decrease and water absorption was increase; (c) The compressive strength of paving block specimens immersed in plain water and peat water showed relatively similar values at 7 and 28 days age, (d). Water absorption in paving block specimens soaked both in plain water and peat water showed relatively similar values at 7 days age, but at 28 days age the specimens immersed in peat water had greater water absorption.

Research of Physical and Mechanical Properties of Fly Ash Ceramics with SiO2 and Al2O3 Nanoparticles as Functional Addition

2021 ◽  
Vol 887 ◽  
pp. 528-535
Author(s):  
V.A. Kalneus ◽  
D.A. Nemushchenko ◽  
V.V. Larichkin ◽  
A.A. Briutov
Keyword(s):  
Mechanical Properties ◽  
Compressive Strength ◽  
Fly Ash ◽  
Water Absorption ◽  
Power Plants ◽  
Bending Strength ◽  
Thermal Power ◽  
Physical And Mechanical Properties ◽  
Ultimate Compressive Strength ◽  
Glass Waste

The article analyses the influence of SiO2 and Al2O3 nanopowders on properties of ceramics consisting of fly ash from thermal power plants, glass waste, and clay binder. Based on studies of physical and mechanical properties of the obtained ceramics (ultimate compressive strength, ultimate three-point bending strength, wear resistance, and water absorption), the paper shows the positive influence of the nanoadditives. The optimal number of SiO2 and Al2O3 nanopowders in the formulation is 0.5 wt. % that has the strongest effect on ultimate compressive strength and water absorption of the fly ash ceramics samples. The direction of further research on improving the properties of ceramic products is an application of the Al2O3 nanopowder as more perspective nanoadditive using clay dispersant.

scholarly journals Combined Effect of Fly-Ash and Ferrochrome Ash as Partial Replacement of Cement on Mechanical Properties of Concrete

2019 ◽  
Vol 93 ◽  
pp. 02008
Author(s):  
Tribikram Mohanty ◽  
Sauna Majhi ◽  
Purnachandra Saha ◽  
Bitanjaya Das
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Compressive Strength ◽  
Fly Ash ◽  
Power Plants ◽  
Thermal Power ◽  
Mineral Admixture ◽  
Waste Materials ◽  
Partial Replacement ◽  
Split Tensile Strength

Due to rapid industrialization extensive quantity of waste materials like fly ash, silica fume, rice ash husk, and ferrochrome ash etc. are generated. Ferrochrome ash is generated from Ferro-alloy industry and fly-ash is produced in thermal power plants are alternative materials which have the potential of being utilized in concrete as a mineral admixture. The present investigation considers the combined influence on strength of concrete using various percentage fly ash and ferrochrome ash as partial replacement of cement. Experiments are carried out to get mechanical properties of ordinary Portland cement by replacement of fly ash by 10%, 20%, 30 % and 3% by ferrochrome ash. Mechanical properties are measured by determining compressive strength, split tensile strength and flexural strength. It can be inferred from the study that a small amount of ferrochrome ash mixed with 30 % fly-ash gives higher compressive strength as compared to fly ash alone. Addition of ferrochrome ash also increases the split tensile strength of concrete. Since ferrochrome ash and fly-ash are both industrial waste, utilization of these waste materials reduced the burden of dumping and greenhouse gas and thereby produce sustainable concrete.

Mechanical Properties and Thermal Conductivity of Lightweight Clay Bricks Fabricated with a Powdered Marble Dust Additive

2018 ◽  
Vol 777 ◽  
pp. 465-470
Author(s):  
Sutas Janbuala ◽  
Mana Eambua ◽  
Arpapan Satayavibul ◽  
Watcharakhon Nethan
Keyword(s):  
Mechanical Properties ◽  
Thermal Conductivity ◽  
Compressive Strength ◽  
Water Absorption ◽  
Bulk Density ◽  
Firing Temperature ◽  
Apparent Porosity ◽  
Clay Brick ◽  
Clay Bricks ◽  
Marble Dust

The objective of this study was to recycle powdered marble dust to improve mechanical properties and thermal conductivity of lightweight clay bricks. Varying amounts of powdered marble dust (10, 20, 30, and 40 vol.%) were added to a lightweight clay brick at the firing temperatures of 900, 1000, and 1100 °C. When higher quantities of powdered marble dust were added, the values of porosity and water absorption increased while those of thermal conductivity and bulk density decreased. The decrease in apparent porosity and water absorption were also affected by the increase in firing temperature. The most desirable properties of the clay bricks were obtained for the powdered marble dust content of 40 vol.% and firing temperature 900 °C: bulk density of 1.20 g/cm3, compressive strength 9.2 MPa, thermal conductivity 0.32 W/m.K, and water absorption 22.5%.

scholarly journals Strength Characteristics of High Strength Concrete (HSC) with and without Coarse Aggregate

2019 ◽  
Vol 9 (2) ◽  
pp. 4701-4704
Keyword(s):  
Mechanical Properties ◽  
Compressive Strength ◽  
Fly Ash ◽  
Flexural Strength ◽  
Silica Fume ◽  
High Strength Concrete ◽  
Mechanical Characteristics ◽  
Coarse Aggregate ◽  
High Strength ◽  
Set Up

This paper aimed to investigate the mechanical characteristics of HSC of M60 concrete adding 25% of fly ash to cement and sand and percentage variations of silica fumes 0%,5% and 10% to cement with varying sizes of 10mm,6mm,2mm and powder of granite aggregate with w/c of 0.32. Specimens are tested for compressive strength using 10cm X 10cmX10cm cubes for 7,14,28 days flexural strength was determined by using 10cmX10cmX50cm beam specimens at 28 days and 15cm diameter and 30cm height cylinder specimens at 28 days using super plasticizers of conplast 430 as a water reducing agent. In this paper the experimental set up is made to study the mechanical properties of HSC with and without coarse aggregate with varying sizes as 10mm, 6mm, 2mm and powder. Similarly, the effect of silica fume on HSC by varying its percentages as 0%, 5% and 10% in the mix studied. For all mixes 25% extra fly ash has been added for cement and sand.

Macroscopic and Microscopic Properties of High Performance Concrete with Partial Replacement of Cement by Fly Ash

2019 ◽  
Vol 292 ◽  
pp. 108-113 ◽  
Author(s):  
Josef Fládr ◽  
Petr Bílý ◽  
Roman Chylík ◽  
Zdeněk Prošek
Keyword(s):  
Compressive Strength ◽  
Elastic Modulus ◽  
Fly Ash ◽  
High Performance ◽  
High Performance Concrete ◽  
Partial Replacement ◽  
Experimental Program ◽  
Second Phase ◽  
Depth Of Penetration ◽  
Cement Replacement

The paper describes an experimental program focused on the research of high performance concrete with partial replacement of cement by fly ash. Four mixtures were investigated: reference mixture and mixtures with 10 %, 20 % and 30 % cement weight replaced by fly ash. In the first stage, the effect of cement replacement was observed. The second phase aimed at the influence of homogenization process for the selected 30% replacement on concrete properties. The analysis of macroscopic properties followed compressive strength, elastic modulus and depth of penetration of water under pressure. Microscopic analysis concentrated on the study of elastic modulus, porosity and mineralogical composition of cement matrix using scanning electron microscopy, spectral analysis and nanoindentation. The macroscopic results showed that the replacement of cement by fly ash notably improved compressive strength of concrete and significantly decreased the depth of penetration of water under pressure, while the improvement rate increased with increasing cement replacement (strength improved by 18 %, depth of penetration by 95 % at 30% replacement). Static elastic modulus was practically unaffected. Microscopic investigation showed impact of fly ash on both structure and phase mechanical performance of the material.

The Effect of Homogenization Procedure on Mechanical Properties of High-Performance Concrete with Partial Replacement of Cement by Supplementary Cementitious Materials

2019 ◽  
Vol 292 ◽  
pp. 102-107 ◽  
Author(s):  
Josef Fládr ◽  
Petr Bílý ◽  
Karel Šeps ◽  
Roman Chylík ◽  
Vladimír Hrbek
Keyword(s):  
Mechanical Properties ◽  
Fly Ash ◽  
Water Content ◽  
High Performance ◽  
High Performance Concrete ◽  
Cementitious Materials ◽  
Supplementary Cementitious Materials ◽  
Partial Replacement ◽  
Depth Of Penetration ◽  
Cement Additive

High-performance concrete is a very specific type of concrete. Its production is sensitive to both the quality of compounds used and the order of addition of particular compounds during the homogenization process. The mechanical properties were observed for four dosing procedures of each of the three tested concrete mixtures. The four dosing procedures were identical for the three mixes. The three mixes varied only in the type of supplementary cementitious material used and in water content. The water content difference was caused by variable k-value of particular additives. The water-to-binder ratio was kept constant for all the concretes. The additives used were metakaolin, fly ash and microsilica. The comparison of particular dosing procedures was carried out on the values of basic mechanical properties of concrete. The paper compares compressive strength and depth of penetration of water under pressure. Besides the comparsion of macro-mechanical properties, the effect of microsilica and fly ash additives on micro-mechanical properties was observed with the use of scanning electron microscopy (SEM) and nanoindentation data analysis. Nanoindentation was used to determine the thickness and strength of interfacial transition zone (ITZ) for different sequence of addition of cement, additive and aggregate. The thickness obtained by nanoindentation was further investigated by SEM EDS line scanning.

Effect of steel slag powder, fly ash, and silica fume on the mechanical properties and durability of cement mortar

2019 ◽  
Vol 9 (9) ◽  
pp. 1049-1054
Author(s):  
Yunxia Lun ◽  
Fangfang Zheng
Keyword(s):  
Mechanical Properties ◽  
Compressive Strength ◽  
Fly Ash ◽  
Silica Fume ◽  
Cement Mortar ◽  
Steel Slag ◽  
Mineral Admixtures ◽  
Partial Replacement ◽  
Slag Powder ◽  
Steel Slag Powder

This study is aimed at exploring the effect of steel slag powder (SSP), fly ash (FA), and silica fume (SF) on the mechanical properties and durability of cement mortar. SSP, SF, and FA were used as partial replacement of the Ordinary Portland cement (OPC). It was showed that the compressive and bending strength of steel slag powder were slightly lower than that of OPC. An increase in the SSP content caused a decrease in strength. However, the growth rate of compressive strength of SSP2 (20% replacement by the weight of OPC) at the curing ages of 90 days was about 8% higher than that of OPC, and the durability of SSP2 was better than that of OPC. The combination of mineral admixtures improved the later strength, water impermeability, and sulfate resistance compared with OPC and SSP2. The compressive strength of SSPFA (SSP and SF) at 90 days reached 70.3 MPa. The results of X-ray diffraction patterns and scanning electron microscopy indicated that SSP played a synergistic role with FA or SF to improve the performance of cement mortar.

Experimental Study on Sustainable Concrete with the Mixture of Low Calcium Fly Ash and Lime as a Partial Replacement of Cement

2011 ◽  
Vol 250-253 ◽  
pp. 307-312 ◽  
Author(s):  
Muthuramalingam Jayakumar ◽  
M. Salman Abdullahi
Keyword(s):  
Compressive Strength ◽  
Fly Ash ◽  
Water Absorption ◽  
Chloride Ion ◽  
Apparent Volume ◽  
Partial Replacement ◽  
Fly Ash Concrete ◽  
Low Calcium ◽  
Chloride Ion Penetration ◽  
Ion Penetration

Even though the use of fly ash in concrete is nowadays a common practice, its relatively slow pozzolanic reactivity hinders its greater utilization; hence efficient methods of activation are on demand. This study was carried out to evaluate the influence of lime as a chemical activator on the mechanical and durability properties of high strength fly ash concrete. Mixtures were made with 0, 30, 40, and 50% of cement replaced by low calcium fly ash. Corresponding mixtures were also made with the same amount of fly ash and addition of 10% of lime to each mixture. For each concrete mixture, slump, compressive strength, water absorption, sorptivity, apparent volume of permeable voids, and resistance to chloride-ion penetration were measured. The results obtained showed that addition of lime improved the compressive strength significantly at all ages. The strength of all the fly ash mixtures containing lime surpassed that of the corresponding Portland cement mix at 60 days. Addition of lime also improved the sorptivity and resistance to chloride-ion penetration of the fly ash concrete. It however increases the water absorption and the volume of permeable voids of the fly ash concrete.